钢筋抽检标准（Inspection standard of rebar）.docVIP

钢筋抽检标准（Inspection standard of rebar） (a) hot rolled steel 1. Group batch rules No more than 60 tons of the same number, same number, same specification, same delivery status, no more than 60 tons. 2. Sampling method Tensile test: two rebar cuts are selected. Two samples, 500mm long. Cold bending test: two samples of two reinforcing bars are selected and the test length is calculated according to the following formula: L = 1.55 * (a + d) + 140 mm In the formula: L - sample length A - reinforcement nominal diameter D - bending diameter of bending test; Click the table for use Strength of steel grades (grades) HPB235 (Ⅰ) HRB335 HRB400 HRB500 The nominal diameter (mm) is 8 ~ 20, 6 ~ 25, 25, 25, 28 ~ 50, 6 ~ 25, 28 ~ 50 Heart diameter d 1a 3a 4a 4a 4a 5a 6a 6a 7a In the cutting sample, the 500mm of the steel bar head should be removed and then removed. (2) hot rolled disk strips of low carbon steel 1. Group batch rules With the same number, same type, same variety, same size, same delivery status, no more than 60 tons for a batch. Sample method: Tensile test: select a set of test samples from the end of the plate. The sample is 500mm long. Bending test: two sets are selected from each end of each set. The sample length is 200mm. In the cut sample, the end of the 500mm should be removed and then cut. (3) cold drawn low carbon steel wire Batch rule A steel wire is tested by plate. The grade b steel wire is inspected with a batch of three plates with a diameter of 5 tons. 2. Sampling method After cutting off from less than 500mm at the end of each plate, take two samples of one stretching, one repeatedly bending, stretching the sample length 500mm, and repeatedly bending the sample length 200mm. (4) cold rolled ribbed bars 1. The mechanical properties and process performance of cold rolled ribbed bars should be tested by plate. After taking 500mm from one end of each plate, two samples shall be taken. The stretching specimen shall be 500mm long and the cold bending specimen