钢渣石灰石复合硅酸盐水泥的研制.pdfVIP

闫加旺，等：钢渣-石灰石复合硅酸盐水泥的研制 设计研究 中图分类号: TQ172 文献标识码: B 文章编号: 1007-0389(2010)01-19-03 钢渣-石灰石复合硅酸盐水泥的研制※ 1 2 2 闫加旺 ，李志强 ，周宗辉 (1. 唐山学院，河北唐山063020 ；2. 济南大学材料科学与工程学院，山东济南250022) 摘 要：通过研究石灰石掺量对钢渣复合水泥强度和安定性等的影响，确定了钢渣—石灰石复合水泥的合理配比，制备了掺量 大、性能优良的钢渣—石灰石复合水泥。结果表明，水泥熟料掺量50%、钢渣35 ％、石灰石10％的钢渣复合水泥，其各项性能指 标均达到32.5R 等级复合硅酸盐水泥国家标准要求。 关键词：钢渣；石灰石；复合水泥 Development of steel slag-limestone composite cement 1 2 2 Yan Jiawang , Li Zhiqiang , Zhou Zonghui (1. Tangshan College, Tangshan 063020, China) Abstract: The influence of the limestone addition on the strength and invariability of the steel slag composite cement was studied and the suitable ratio of the steel slag-limestone composite cement was determined. And steel slag-limestone cement with a large amount addition and good property was produced. The research results show that all performance indices of the steel slag-limestone composite cement, containing 50% cement clinker, 35% steel slag content and 15% limestone content, reach to the requirements of national stan⁃ dards for 32.5R composite portland cement. Keywords: steel slag; limestone; composite cement 通过测定复合水泥的强度、安定性等性能并且利用 0 前言 XRD 分析水泥水化产物的组成，利用扫描电镜观察 钢渣是炼钢生产过程的废渣，它凝聚了炉料被 水化产物形貌、微观组织结构，分析石灰石掺入量对 氧化后生成的氧化物及硫化物等，主要来自金属炉 钢渣水泥性能的影响，制得钢渣—石灰石复合水泥。 料中各元素被氧化后生成的氧化物、被侵蚀的炉衬、 1 试验原料及方法 补炉材料和为调整钢渣性质而特意加入的造渣材料 [1-3] （如石灰石、白云石、铁矿石、萤石、硅石等） 。每生 济钢转炉罐闷钢渣，石灰石、二水石膏、水泥熟 产1t 粗钢约排放15% 的钢渣，我国积存钢渣已有4 料来自莱芜连云水泥集团有限公司。化学激发剂为 [4] 亿t 以上，且每年仍以数千万吨的排渣量递增 ，但