废旧电脑主板回收Cu.docVIP

废旧电脑主板中Cu、Al的湿法研究 摘要：本论文采用浸出浸出时间、硫酸和双氧水用量、浸出温度等工艺条件浸出时间4h，双氧水用量0.2mol，硫酸用量0.5mol，温度为70℃97.5％关键词：废旧电脑主板，湿法浸出，Cu、AlHydrometallurgical Leaching of Copper and Aluminium from Waste Computer Board－A Study , Central South University,Changsha 410083,China) Abstract：The waste computer board was crushed to smaller than －0.85mm by crusher and initially separated into 25% conducting and 75% nonconducting materials by electrostatic separator. The conducting materials ,which contained copper and aluminium ,was leached by sulphuric acid and hydrogen peroxide . The influences of leaching time ,reaction temperature and the amount of sulphuric acid and hydrogen peroxide was investigated. The result indicated that the favorable condition is 0.5 mol sulphuric acid (98%) and 0.2 mol hydrogen peroxide(30%) at 70℃ for four hours. Under this condition ,the dissolution of copper and aluminium is 99.6% and 97.25% respectively . The reagents are nontoxic,cheap and easily attainable and the equipments are simple .The whole operation is convenient .No toxicant was produced during the course of reaction . Key words：waste computer board ; hydrometallurgical leaching ;copper ; aluminium 在电脑主板中富含大量有害化学元素，例如铜、铝、汞、金等金属，若得不到妥善处置将对人类健康和环境安全构成极大的危害，同时，也是对资源的巨大浪费据统计1吨PC机电子废料中的含金量比17吨金矿石中的含金量还多[1]。而在当今社会中，为了满足需求，计算机产品中使用了数量巨大且类型多样的材料，同时电脑需求数量剧增，更新速度加快，废弃电脑日益增多，贵金属和稀有金属浪费日趋严重，正是在环境和资源双重要求下，对废旧电脑的回收势在必行。 对废旧电路板的处理现在常用的方法有固化法、焚化法、热裂解法、物理分离法，但这些方法都各有其弊病例如热裂解法可以得到较纯的塑料，但是条件要求高，能耗高，物理方法虽然金属回收率较高，但无法实现金属分离。而湿法冶金技术方法简单、设备要求不高，其基本原理是利用废电脑以及其配件中的绝大多数金属（包括金等贵金属和贱金属）能在硝酸，硫酸，王水等强氧化性介质中溶解而进液相的特性，绝大部分贵金属和其他金属进入液相与电脑及其配件中的其他物料分离，然后从液相中分别回收各种金属。 1 试验设备及其试剂、原材料 1.1 设备 鄂式破碎机；塑料破碎机SWP-260，青岛臻昌盛塑料机械厂制造；标准筛振筛机XSB-70BΦ200，柳州探矿机械厂制造；振动磨机XZM100，武汉探矿机械厂制造；高压电选机YD3030—116；增力电动搅拌机JB50—D型；电热恒温水槽DK—8D型； 1.2试剂 浓硫酸98％湖南药剂总厂生产双氧水30％，株洲化工制药厂生产。 1.3原材料 首先要对废电脑进行人工拆卸并进行分类，通过鄂式破碎机和塑料破碎机将主板破碎到，进行电选，分离导体，再用振动磨样机对导体进行粉磨至－0.075mm，得到浸出原料。 X－射线分析表明物料中的Cu、Fe、Al主要以金属单质的形式存在，见图1；热重分析表明原料中含PVC、ABS等约为6.3％，见图2；原料中各种金属含量见表1。