GBT2423.17-93中型盐雾试验标准(NSS)（Standard gbt2423.17-93 medium salt spray test standard (NSS)）.docVIP

GBT2423.17-93中型盐雾试验标准(NSS)（Standard gbt2423.17-93 medium salt spray test standard (NSS)） National standard: GB/T2423.17-93 medium salt spray test standard (NSS) Basic environmental test procedure for electrical and electronic products Test Ka: salt spray test method 1 test purposes This standard is used to assess the resistance to salt, fog and corrosion of materials and their protective coatings, as well as to compare the quality of similar protective coatings To evaluate the salt fog resistance of some products. This standard is not intended as a universal corrosion test method. 2 test equipment 2.1 materials used in the manufacture of test equipment must be salt spray resistant and do not affect test results. 2.2 conditions in the test equipment shall be kept within the limits specified in the third chapter of this standard. 2.3 salt mist shall not be sprayed directly on the test sample. 2.4 the water collected in the top and the wall of the test equipment shall not be dripped on the test sample. 2.5 the pressure inside and outside the test equipment must be balanced. 3 test conditions The 3.1 salt solution is configured with sodium chloride (above pure chemical) and distilled water, with a concentration of 5 + 0.1% (weight). Collection fluid after physicochemical removal The baffle shall not be reused. 3.2 the pH value of the salt solution before atomization is between 6.5~7.2 (35 DEG C). When the salt solution is configured, dilute hydrochloric acid above the chemical purity is allowed Sodium hydroxide solution to adjust the pH value, but the concentration must comply with the provisions of the 3.1. 3.4 using a funnel with a surface area of 80cm2 to collect the salt fog settlement of continuous atomization 16h, and the sedimentation rate in any position in the effective space is: 1.0~2.0ml / h.80cm2. 3.5 this standard adopts continuous atomization, the recommended standard test time is 16, 24, 48, 96, 168, 336, 672h. 3.6 when atomizing, it is necessary to preve