镁合金塑性变形过程中孪生行为的研究.PDF

下半月出版 Material Heat Treatment 料热处理技术 镁合金塑性变形过程中孪生行为的研究 李小飞, 左汝林, 林崇智 (重庆大学 材料科学与工程, 重庆 400045) 摘 要 结合国内外对镁合金塑性变形过程中孪生行为的研究进展 阐述了孪生的晶体学以及几何位向学 分析了 孪晶与孪晶之间以及孪晶与滑移之间的相互作用曰探讨了影响孪生的几方面因素 包括应变路径尧形变温度尧应变速率尧 晶粒尺寸以及晶粒取向遥 关键词 合金曰孪生曰塑性变形 中图分类号 TG 146.22 文献标识码 A 文章编号 Research on Twinning Behavior in Plastic Deformation of Magnesium Alloy LI Xiaofei, ZUO Rulin, LIN Chongzhi (College of Materials Sc ience and Engineering, Chongqing Univ ers ity, Chongq ing 400045, China) Abstract 院Combining the domestic and overseas development of plastic deformation research in magnesium alloy, the crystallology and geometry of twinning were overviewed. Then, the interaction between twins and between slip dislocations and twins were analyzed. The effects of several factors on the twinning, including strain path, temperature, strain rate, grain size and crystal orientation, were emphasized. Key words 院magnesium; twinning; plastic deformation 及其合金是目前可用的最轻的金属结构材 1 镁合金孪生的概述 料 具有密度低尧比强度高和阻尼减震性好等优点 [1-2] 孪生是晶体的一部分沿一定的晶面(孪生面)和 在汽车工业领域显示出了广阔的应用前景 遥 镁合 金密排六方晶格的特点 限制了其在低温下的塑性 一定的晶向(孪生方向)相对于另一部分晶体做均匀 变形能力 一般室温下变形只能启动基面滑移 而柱 的切变 切变部分发生晶格转动 与未切变部分形成 面和锥面滑移则很难启动 这是因为在变形过程中 镜面对称遥 孪生切变具有单向性 即沿孪生方向 1 基面滑移所需的临界剪切应力(CRSS)较柱面和锥 的相反方向则不能发生孪生遥 面滑移要 遥然而 基面滑移仅仅只能提供垂直于C 在HCP 结构的纯 及其合金中 孪生是一种重 轴方向的应变 这就需要孪生来协助完成C 轴方向 要的晶内变形机制遥 在一定的温度范围内 滑移尧孪生