硬铝合金粘接接头性能测试分析.pdfVIP

金属铸锻焊技术lcas血g·F0rging·Welding 2伽l8年2月 硬铝合金粘接接头性能测试分析 孙礼娜，张鑫，徐全伟，王淋群 (河南科技大学材料科学与工程学院，河南洛阳471003) 摘 要：选用适宜的金属粘接剂，制备了硬铝合金粘接接头，并对不同粘接工艺条件下接头的剪切强度进行了测 试比较。结果表明：当粘接剂中A胶、B胶两组分的质量配比为3：l时，接头强度较高，且在该比例下。粘胶层固化10h 后，接头可达到最高剪切强度。 关键词：硬铝合金；粘接；剪切强度；质量配比：固化时间 中图分类号：TG457．14 文献标识码：A 文章编号：lOO1．3814(2008)03-0076．02 Testing and Analysis on Property of Hard-AI Alloy Adhesive Joint SUN Lina，盟 ANG Xin，XU Quanwei．WANG Linqun (Co／／ege ofMaterials Scieme and Engineering,Heneat University ofScience and Technology,Luoyang 471003。China) Abstract：Using appropdate metal adhesive，the adhesive joint ofhard-Al ahoy was prepared．And the shear strength of the joints at different procedure conditions were tested and compared．The results show that the ioint strength is higher when the proportion by weight of the composition of glue A and glue B is 3：1；and at the same proportion,the shear strength is the highest when the solidification time is over lOh ． Key words：hard-Al alloy；adhesive；shear strength；proportion by weight；solidification time 由于铝及铝合金的化学性质活泼．加之其导 图 l所示。 热性强和线胀系数大，所以在对其进行熔化焊接 时容易造成不熔合和翘曲变形现象．且其表面氧 ．-卜 吲 化膜因与铝密度接近，容易成为焊缝金属夹杂物， LJ 若氧化膜吸收了过多水分还易在焊缝中形成气 图1．试样形状与尺寸(粘接前) 孔。因此，利用熔焊的方法不易获得可靠的铝及其 Fig．1 Shap~and sizeofsamples(before adhering) 合金接头【l】。 1．2 粘接试验 粘接是人类最早使用的连接方法之一，现代 在该粘接剂三组份中，A、B两胶起主要的连 粘接技术已广泛应用于从日常生活到机械、轻工、 接作用，两者按一定的质量比例混合均匀后使用。 无线电、建筑、航天等各个领域。本次试验即从市 面胶为铝亮色，待接头粘胶层固化后即可将