45#介绍与调质（Introduction and conditioning of 45#）.docVIP

下载本文档

4
0
约9.03千字
约 7页
2017-08-02 发布于河南
举报
版权申诉

45#介绍与调质（Introduction and conditioning of 45#）.doc

1、原创力文档（book118）网站文档一经付费（服务费），不意味着购买了该文档的版权，仅供个人/单位学习、研究之用，不得用于商业用途，未经授权，严禁复制、发行、汇编、翻译或者网络传播等，侵权必究。。
2、本站所有内容均由合作方或网友上传，本站不对文档的完整性、权威性及其观点立场正确性做任何保证或承诺！文档内容仅供研究参考，付费前请自行鉴别。如您付费，意味着您自己接受本站规则且自行承担风险，本站不退款、不进行额外附加服务；查看《如何避免下载的几个坑》。如果您已付费下载过本站文档，您可以点击这里二次下载。
3、如文档侵犯商业秘密、侵犯著作权、侵犯人身权等，请点击“版权申诉”（推荐），也可以打举报电话：400-050-0827(电话支持时间：9:00-18:30)。
4、该文档为VIP文档，如果想要下载，成为VIP会员后，下载免费。
5、成为VIP后，下载本文档将扣除1次下载权益。下载后，不支持退款、换文档。如有疑问请联系我们。
6、成为VIP后，您将拥有八大权益，权益包括：VIP文档下载权益、阅读免打扰、文档格式转换、高级专利检索、专属身份标志、高级客服、多端互通、版权登记。
7、VIP文档为合作方或网友上传，每下载1次，网站将根据用户上传文档的质量评分、类型等，对文档贡献者给予高额补贴、流量扶持。如果你也想贡献VIP文档。上传文档

45#介绍与调质（Introduction and conditioning of 45#） The concept of No. 45 steel: No. 45 is the term GB in JIS. It is called S45C in, and ASTM is called 1045080M46, and DIN is called C45. Domestic often called 45 steel, also known as oil steel.. In general, the market hot spot mostly. Cold rolled specification 1.0~4.0mm between. Quenched and tempered hardness of No. 45 steel: Heat treatment process for quenching and tempering of 45# (number) steel and 40Cr steel Quenching and tempering is the double heat treatment of quenching and high temperature tempering, the purpose is to make the workpiece have good comprehensive mechanical properties. Quenched and tempered steel has two major categories: carbon quenched and tempered steel and alloy quenched and tempered steel. Carbon steel or alloy steel, the control of carbon content is relatively strict. If the carbon content is too high, after quenching and tempering the strength of the workpiece is high, but the toughness is not enough, such as carbon content is too low, toughness and lack of strength. In order to make the quenched and tempered parts get good comprehensive performance, the total carbon content is controlled at 0.30~0.50%. During quenching and tempering, the whole section of the workpiece is quenched and the microstructure of the workpiece is obtained with fine acicular quenched martensite. By tempering at high temperature, the microstructure with uniform tempered bainite is obtained. It is impossible for a small factory to do metallographic analysis of each furnace. It is generally used only for hardness testing. That is to say, the hardness of the quenched material must be reached by the quenching hardness of the material, and the hardness after tempering shall be checked according to the requirements of the drawing. The operation of the workpiece quenching and tempering process must be carried out in strict accordance with the process documents. We just make some comments on how to implement the process. 1 、 N