高韧性高铬铸铁衬板的研制与应用（Development and application of high toughness high chromium cast iron liner）.doc

高韧性高铬铸铁衬板的研制与应用（Development and application of high toughness high chromium cast iron liner） The high toughness of high chromium cast iron lining board development and application - The high toughness of high chromium cast iron lining board development and Application A preface. According to statistics, Chinas annual consumption of metal materials is about 3 million tons, of which only lining consumption of metallurgical mines reached 100 thousand tons. At present, Chinas various types of mine mill selection for mine mill and other processing equipment in the liner wearing parts generally used ZGMn13 high manganese steel. This kind of vulnerability is in use to withstand impact and abrasive wear, the material should have good anti-wear and impact toughness. The impact toughness of high manganese austenitic high ZGMn13 (AK 200J/cm2), the original hardness is less than HB230, but in high impact load under the surface layer can produce a hardening effect, the surface hardness of up to HRC42-48, and the center still maintain excellent toughness. But if the service when the impact energy is not enough, the impact of high manganese austenitic steel surface hardening effect can not be fully produced, high manganese steel surface is not up to the high hardness, the body is soon wear. At the same time, the high manganese steel yield limit (0.2) is low (about 350Mpa), in use, especially the use of pre plastic deformation of workpiece. The ball mill liner and grinding media (such as ball) between a hardness, grinding medium hardness should be higher than the general lining hardness of about HRC3 is appropriate, but the low chromium cast iron, at present a lot of factories use the high chromium cast iron grinding ball hardness is higher than that of high manganese steel plate hardness. High manganese steel under low impact load of the above problems often lead to the toughness and wear resistance of workpiece is more than enough, wear quickly, and the deformation is serious, re