混凝土弊病（Concrete defects）.docVIP

混凝土弊病（Concrete defects） The appearance of defects in concrete engineering A honeycomb (1) with inaccurate measurement, aggregate grading is not good; (2) uneven stirring; (3) template leakage; (4) the vibration is not enough or leakage of vibration; (5) a pouring concrete layer is too thick, not clear, concrete transfer is not clear, unable to grasp the quality of the vibration; (6) free fall height exceeds the concrete segregation and gravel pile driving; (7) the vibrator is damaged, or when the power failure caused by leakage of vibration monitoring; (8) the vibration time is not sufficient, the bubble is not excluded. Two, Ma (1) the same honeycomb reasons; (2) the template cleaning is not clean, or early form removal, template adhesion; (3) release agent brushing unevenness or leak brush; (4) no watering wood wet concrete surface, dehydration, powder; (5) the pouring time is too long, the template hanging ash too much not cleared up, causing the surface layer is dense; (6) the vibration time is not sufficient, the bubble is not excluded. Three holes (1) the same cellular reason; (2) reinforced concrete aggregate is too thick, too thick, not easy to dust, not easy to vibrate; (3) the hole bottom, no concrete template outlet within the balloon. Four, reinforcement (1) the same honeycomb reasons; (2) no steel skeleton processing, the top post template; (3) the lack of protective layer pad; (4) bar too close; (5) no reinforcement measures, reinforcement displacement positioning punch. Five, rot (1) template root gap blockage lax leakage; (2) before pouring concrete with no stone mortar not below than the same ingredients; (3) the workability of concrete, water cement ratio is too large stone sink; (4) pouring height is too high, a centralized concrete material, concrete or stones piled high on the rush; (5) vibrator is not real; (6) mold clean-up net, wet is not good. Six, missing edge off angle (1) the template design is not considered to prevent stripping off angl