V01．33No．6 ElectricPower DeC．2011 Heilongjiang 带涂层工件磁粉检测的试验分析 王珍 (黑龙江省火电第三工程公司，黑龙江哈尔滨150016) 摘要：介绍了磁粉检测铁磁性材料表面和近表面缺陷原理，通过理论和实验相结合的方法分析了涂层对磁粉检测 的影响。试验分析结果表明，只要其涂层厚度不超出一定范围，带涂层进行磁粉检测其检测灵敏度仍然能够满足检 验的需要。 关键词：涂层；磁粉探伤；漏磁场 中图分类号：TGll5 文献标识码：A 文章编号：1002—1663(2011)06—0470一03 material弼tha of Ferromagnetic coatingshapedmagneticparticletesting WANGZhen ThermalPowerNo．3 (Heilongjiang EngineeringCompany，Harbin150016，China) describesthe detectionof materialsurfaceandnearsurfacedefectsin Abstract：This paper magnetic ferromagnetic acombinationoftheoreticaland methodsof ofthe of onthe coating principle，through experimentalanalysisimpact conclusion asthe thicknessdoesnotexceedacertain is：as magneticparticleinspection，the long coating range its isstillabletomeet needs． with for of detection coatingsmagneticparticletesting sensitivity inspection flux Keywords：coating；magneticparticleinspection；magneticleakage 于不连续性的存在，使工件表面和近表面的磁感应 0 引 言 线发生局部畸变而产生漏磁场，吸附施加在工件表 磁粉检测因其检测成本低、能快速检测出铁磁 面的磁粉，在合适的光照下形成目视可见的磁痕， 性材料的表面和近表面缺陷、缺陷检测重复性好等 从而显示出不连续性的位置、大小、形状和严重程 优点而得到广泛应用，它是RT、UT、MT、PT无损检 度。 ． 测方法中对表面裂纹检测灵敏度最高的检测方法。 缺陷处产生漏磁场是磁粉检测的基础，漏磁场的大 2涂层对磁粉检测的影响 小对磁粉检测缺陷的灵敏度至关重要。影响漏磁