芯子宽厚比对铝蜂窝夹层结构平压强度的影响 章摇 妮摇 摇 卢克非摇 摇 崔文龙 (航天材料及工艺研究所,北京摇 100076) 文摇 摘摇 用正六边形代替实际蜂芯,推导了夹层结构的平压强度与芯子宽厚比的关系,并对八种规格的芯 子平压强度进行统计,统计结果虽然与推导的结果有偏差,但规律却是一致的,即蜂窝夹层结构的平压强度随 着芯子宽厚比d/ t 增大呈负指数减小。s 关键词摇 铝蜂窝,夹层结构,宽厚比,平压强度 中图分类号:V45 DOI:10.3969/ j.issn.1007-2330.2016.02.008 Effection of Ratio of Width to Thickness of Aluminum Honeycomb Sandwich Structure of Flatwise Compression Stress ZHANG Ni摇 摇 LU Kefei摇 摇 CUI Wenlong (Aerospace Research Institute of Materials Processing Technology,Beijing摇 100076) Abstract摇 Using the hexagon instead of the actual honeycomb core,the flat compression strength of sandwich structure and its relationship with the width to thickness ratio was deduced.Eight kinds of specifications of core flat compressive strength were evaluated. Statistical results revealed that although there are deviations from the deduced results,the law is consistent,namely honeycomb sandwich structure of flat compression strength decreases exponen鄄 tially with the increase of core width to thickness ratio d/ t .s Key words摇 Aluminumhoneycomb,Sandwichstructure,Ratioofwidthtothickness,Flatwisecompressionstress 0摇 引言 平压强度与芯子材料类型、形状规格和芯子密度等都 夹层结构在复合材料领域是一种常见的结构,通 [4 ] 有密切关系 。 常由蒙皮和芯体组成,具有比强度、比模量高,密度低 和透波性好等特点。 在航空、航天、船舶、建筑、桥梁 等领域广泛应用,尤其在航空和航天领域应用最为广 泛,如大型运载火箭整流罩、仪器舱、卫星支架、贮箱 共底,卫星的电气结构板、天线反射器、太阳能电池阵 [1] 基板,载人返回舱侧壁、防热大底以及天线罩等 。 夹层结构芯子包括泡沫、蜂窝和软木等轻型材 料。 由于夹层结构的组成复杂,蒙皮材料的强度和模 量高于芯材,为反映夹层结构的真实性能,其试验方 图1摇 平压强度测试示意图 [2] 法较为复杂 ,而平压试验方法是其中较为简单的 Fig.1摇 Schematic diagram of flatwise 方法。 夹层结构或芯子的平压强度是通过在垂直于 compression Strength tset 芯材平面(即厚度方向