MLCC抗弯曲强度研究与应用.pdf

Technology 技术 MLCC抗弯曲强度研究与应用 杨善明 张成成 崔斌 （格力电器（合肥）有限公司 安徽合肥 230600） 摘要： 本文结合空调用片状多层陶瓷电容器（简称MLCC）本体断裂问题，采用外观观察和金相分析方法，对绝缘电阻偏低的MLCC进行失 效原因分析，结果表明：MLCC失效是因电路板过度弯曲使电容器受到过大的机械应力，样品失效后裂纹一般位于器件两端的电极，沿着 45°角向器件内部扩展。基于对MLCC的分析及研究，为避免外部机械应力导致电容器失效，故采用软端子或“S”型结构，从而提高MLCC 的抗弯曲强度，提高其使用可靠性。 关键词： MLCC；抗弯曲强度；机械应力；可靠性 Research and use for multi-layer ceramic capacitor buckling strength YANG Shanming ZHANG Chengcheng CUI Bin (Gree Electric Appliances,inc.of Hefei Hefei 230600) Abstract： This article is related to the problems on air/con used Multi Layer Ceramic Capacitor (MLCC) body crack, by using outlook inspection and Electron metallographic analysis method to analyze the low value of isolation resistances of MLCC. The result shown: MLCC failure is due to PCB over bending which happened over mechanical stress on capacitor, failure samples crack normally located at the components both 2 electron edge pin side, from the 45deg of the body and extend to the inner body. After the analysis and the root cause, to avoid over mechanical stress for the damage on the capacitor, it should be used soft terminal or S shape structure to improve the MLCCs bending ability and improve the utility of the reliability of the capacitor. Keywords： MLCC; Bending ability; Mechanical stress; Reliability 1 引言 旦MLCC发生故障，将导致空调功能失效。因 械应力导致本体开裂，同时，相关资料显示，行 MLCC，片状多层陶瓷电容，现在已经成为 此，对失效产品进行失效分析，揭示其失效原因 业中也存在类似现象。本文则通过MLCC的抗弯 了电子电路最常用的元件之一，具有容量大、体 及失效机理，并提出相应的改进和预防措施，具 曲能力、失效模式分析及改善措施，对MLCC抗 积小、电容量稳定、耐高温耐湿性好和易于表面 有非常积极的现实意义。 弯曲强度进行研究。 安装等特点，被广泛应用于空调整机的高频滤 MLCC 的失效原因包括本体开裂、介质空 波、电源退耦和旁路等电路中，MLCC结构示意 洞、分层[2] 以