电动机定子铁损试验.docVIP

电动机定子铁损实验的探讨 摘要：铁损是电动机能量损失之一，不仅影响电动机效率、功率因数，而且可能因铁芯内部硅钢片短路产生妨碍电动机安全运转的局部过热点，加速铁芯绝缘和定子线圈绝缘的老化，严重时可能造成铁芯烧损及线圈击穿事故。所以，在检修电动机时，尤其是出现扫膛状况时，为检查铁芯受损情况，需进行定子铁损试验。对于大型电动机，这是检查中必不可少的试验项目。 关键字：绝缘，扫膛，铁损试验 Abstract:Iron loss is one of the motor energy loss, not only affect the motor efficiency, power factor, but also may impede the safe operation of local hot spots generated by the motor iron core internal short circuit of silicon steel slice, accelerate the insulation core and stator coil insulation aging, may cause the iron core loss and winding breakdown accident severity. In the maintenance of the motor, especially the sweep chamber condition, in order to check the damage situation of iron core, stator iron loss test. For large motor, it is essential to test the project inspection. Key words:insulation, sweep, chamber, iron loss test概述 本文所论述的电动机定子铁芯铁损试验就是其中之一。电动机定子铁损试验是检验电动机定子铁芯质量的重要方法，也是检验铁芯自身绝缘性能的重要工序。铁芯表面和片间绝缘比较薄弱。在检修过程中尤其是进入定子膛内检修一定要小心仔细，防止工具及一些硬物与铁芯直接接触。在达到试验周期和必要时一定要进行铁损试验，lT和供电电源的频率为50Hz。 下图为电动机定子铁损试验原理图，图中WC为励磁线圈，WM为测量线圈，为使测量线圈处铁心磁感应强度接近整个轭部圆周磁感应强度的平均值，励磁线圈与测量线圈应互相垂直，且均匀地绕在铁心上；电流表A经电流互感器或钳形电流表测励磁电流，电压表V1测二次感应电压（U2），电压表V2测电源电压（U1），低功率因数瓦特表W测损耗功率PFe，其电流回路与励磁线圈串联，电压回路则接到测量线圈，减少励磁线圈漏磁压降和电阻的影响。 试验持续时间为90分钟。用可以测量电流、电压和功率的组合仪表每隔15分钟分别测量一次铁芯损耗及电流、电压值。并用红外热像仪测量铁芯各部位温度；先用红外测温仪测量铁芯冷态温度，合上电源10分钟后开始用红外测温仪扫描膛内各处温度，找出铁芯温度较高与较低的点。以后每隔15分钟用红外测温仪对铁芯温度进行观测，着重观测铁芯温度较高与较低的点，直至90分钟结束。 图1 定子铁损试验原理图 试验前相关数据采集与计算 2014年月12日（K）(V) 380/660V 额定电流(A) 55.2/32A 定子外径(Da) 0.3m 定子内径(Di) 0.16m 齿 高(hz ) 0.01m 铁心总长(L ) 0.17m 叠压系数(k) 0.96 硅钢片牌号 50WB340 额定转速(r/min) 2950r/min 功率因数 0.9 实验前相关计算 定子铁心有效长度 Lef=KL=0.17×0.96=0.1632(m) 定子铁心轭部高度 ha=(Da-Di)/2-hz=(0.3-0.16)/2-0.01=0.06(m) 定子铁心轭部截面积 S=L×ha=0.06×0.1632=0.0098(m) 测量绕组每匝感应电势 E=4.44fBS=4.44×50×1×0.0098=2.1756(V) 励磁线圈取19匝，此时励磁电压值为 U= W1E=19×2.1756=41.3364(V) 铁