Densification Behavior of Rhenium Alloy using （铼合金的致密化行为使用）.pdfVIP

J. Kor. Powd. Met. Inst., Vol. 21, No. 1, 2014 DOI: 10.4150/KPMI.2014.21.1.7 PM리뷰 Densification Behavior of Rhenium Alloy using Master Sintering Curve a b c Dong Yong Park, Yong Jun Oh , Young Sam Kwon , Seong Taek Lim , and Seong Jin Park* Department of Mechanical Engineering, Pohang University of Science and Engineering (POSTECH), Pohang 790-784, Korea aDivision of New Materials Engineering, Hanbat National University, 125, Daejeon 305-719, Korea b CetaTech, Inc. TIC 296-3, Sacheon-si 664-953, Korea cAgency for Defense Development, P.O.Box 35-5, Daejon 305-600, Korea (Received February 12, 2014; Accepted February 17, 2014) ································································································································································································································ Abstract This study investigated the densification behavior of rhenium alloys including W-25 wt.%Re and Re-2W- 1Ta (pure Re) during sintering. The dilatometry experiments were carried out to obtain the in-situ shrinkage in H2 atmo- sphere. The measured data was analyzed through shrinkage, strain rate and relative density, and then symmetrically treated to construct the linearized form of master sintering curve (MSC) and MSC as a well-known and straightforward approach to describe the densification behavior during sintering. The densification behaviors for each material were ana-