混凝土徐变力学1.pptVIP

混凝土徐变力学 北航：黄 达 海 第一讲：绪论 为什么要学习混凝土徐变力学？ 混凝土徐变力学包括哪些内容？ 混凝土徐变力学学习方法？ 什么是徐变？ Deformation; Displacement; Defluxions; Slope; Strain; Time-dependent deformation; Shrinkage Creep 什么是徐变？ Concrete creep----a part of time-dependent deformation; Shrinkage creep and basic creep No moisture change Our interesting is aimed on “concrete creep”. Open the door! How the experts face to it? Half-theory and half-experience way! Time-depended deformation time curve humidity dependence size dependence: size dependence: Age dependence: Age dependence: temperature dependence ---time, (in days), representing the age of concrete; -------effective age (maturity) when drying begins; duration of drying; ultimate shrinkage; -relative humidity of environment shrinkage half-time; -effective cross-section thickness in millimeters; drying diffusivity of nearly saturated concrete at reference temperature based on the activation energy of moisture migration; activation energy; gas constant; shape coefficient; reference temperature (chosen as 23C for all the tests) absolute temperature composition dependence and strength dependence Chinese way How to deal with Basic creep? Not the physical way, but the mechanical way! 什么样的结构特别关注变形与总变形？ Long span concrete structure; Tall building concrete structure; High stress level concrete structure Pre-stressed concrete structure; Massive concrete structure; Support structure for metal structure; 为什么要学习混凝土徐变力学？ 土木工程主要材料----石、钢、木、混凝土； 木材受荷能力有限，总徐变量有限，对结构整体受力状态与变形状态的影响小； 钢材密度大，本身基本不产生徐变； 石材与混凝土密度接近，加上石材构造面的影响，徐变量与混凝土基本相当； 结构工程的飞速发展对材料研究提出新的要求 在新的条件下，如磁悬浮列车的托梁，在日常温度变化下，具有可以控制的挠度。是还在继续研究的阶段； 对膨胀混凝土的应用，也要求对徐变使膨胀的损失定量化！ 南京化工大学唐明述院士； 中南院在龙滩上的试验； 沙老河的试验； 朱伯芳的态度； 国内试验研究情况等 考虑徐变后拉应力反而增大了？ 用不同部位徐变效果不同，不同时间，徐变效果不同, 是十分模糊也没有什么意义的。 因为，徐变实际上是材料自身调整应力的过程，也是地基调整应力。 我的导师刘光庭 清华大学多轴徐变实验的设计具有一定水准。 徐变实验要求有良好的温度与湿度控制。 唯理上的解释 一个流动模型与一个弹簧模型串联，形成一个麦克斯伟模型，再将许多麦克斯伟并联，形成实用模型。 但这两个模型在模型参数决定方面是不同的， 因此，我们常常选择使用麦克斯伟模型。 如果处理不当 使用寿命下降； 徐变导致应