大型耐磨蠕墨铸铁的生产实践.PDF

2014 中国铸造活动周论文集 大型耐磨蠕墨铸铁的生产实践 范应光，陈汝霞 （广西机电职业技术学院，广西南宁 530007 ） 摘要： 本文针大型蠕墨铸铁甘蔗压榨辊的工况条件、性能要求，研制了相应的耐磨蠕墨铸铁合金成分配方， 设计了适应于铸造大型蠕墨铸铁件的蠕化工艺方法、熔炼设备及浇注工艺要求，论述了大型耐磨蠕墨铸铁 件生产技术原理及方法。 关键词：蠕化剂；蠕化处理；大型蠕墨铸铁 Production Practice of Large Wear-resistant Compacted Graphite Cast Iron FAN Ying-guang, CHEN Ru-xia （Guangxi technological college of machinery and electricity, Nanning 530007, Guangxi ） Abstract: This needle large sugarcane roller compacted graphite cast iron working conditions, performance requirements ，Relative composition formula is developed ，Design adapted to the casting of large of creep process method for compacted graphite iron castings, melting equipment and pouring process requirements ，Commented on the large principle and method of wear-resistant vermicular iron castings production technology. Key words: creep agent; creep of processing; large compacted graphite cast iron 甘蔗压榨辊是糖厂的重要关健零部件，随着糖业生产的集约化，我国出现了日榨 2 万多吨甘 蔗的大型糖厂,甘蔗压榨辊直径达 1200mm、厚度 320mm，单件毛坯重达 22 吨，属大型铸铁件。 广西某糖机制造有限公司是以其生产甘蔗压榨辊作为该厂的主导支柱产品，该厂以前生产的甘蔗压 榨辊是用普通灰口铸铁生产，由于辊齿面磨损大、易崩齿、寿命短面临着逐步失去了市场竞争能力 的风险。而耐磨蠕墨铸铁甘蔗压榨辊在甘蔗压榨机中有明显的性能优势，自从该厂与广 西机电职业技术学院有关技术人员联合技术攻关，多次研究试验后，生产出大型蠕墨铸铁甘蔗压榨 辊，该厂的糖机设备产品市场竞争能力得到了提高，夺回了市场销售的份额，产品远销海内外。 1 磷硼蠕墨铸铁压榨辊的生产工艺 1.1 熔化设备 熔化设备为 10t ／h 的燃油热风化铁炉（两座），这种大型化铁炉炉子是以重油为燃料，燃烧室 与前炉共为一体，前炉与炉膛连为一体的结构，铁水基本上不增碳。化学成分较稳定(表 1 所示) 。由于重油 是在储蓄铁水的前炉喷火燃烧的，有利于铁水过热，并且前炉燃烧火焰较均匀、稳定，保证了铁液的 迅速升温迅速而有保证，铁水温度可高达 l450℃。 1.2 化学成分 蠕墨铸铁化学成分见表 1。 1 2014 中国铸造活动周论文集 表 l 蠕墨铸铁化学成分 Table1 Chemical constituents of compacted graphite cast iron (wB/%) 名称 C Si Mn S P Cu