不锈钢结构抗火性能探究综述.docVIP

不锈钢结构抗火性能探究综述摘要：火灾高温对建筑结构有显著影响，极易引起建筑物倒塌。不锈钢具有耐腐蚀性和造型美观等优点在结构中得到越来越广泛的应用，不锈钢结构和普通钢结构类似，在火灾高温下容易破坏。介绍了目前国内外关于不锈钢高温下的材性试验研究和应力应变关系，的试验和理论研究；指出了目前研究中存在的问题并对未来的研究趋势进行了展望。 关键词：不锈钢；抗火；研究现状 Abstract: High temperature of fire has significant influence on the building structures and extremely easily causes collapse of buildings. Stainless steel has good corrosion-resistant and beautiful shape and hence it is more and more widely used in structures. Stainless steel are similar with normal steel, the structures are sensitive to damage in fire. The current research statuses on material properties and strain-stress relationship of stainless steel at elevated temperature were summarized. The problems in current research were pointed out and the research trend was prospected. Keywords: Stainless steel; fire resistance; research status 中图分类号：TF764+.1文献标识码：A 文章编号： 0. 引言 不锈钢在冶炼过程中大量添加了Cr、Ni、Mn、Mo等合金元素，这些元素的加入使得不锈钢的物理力学性能明显区别于碳素钢[1]。力学性能方面：首先，不锈钢在较低的应力应变下就表现出非线性性能，其应力应变关系通常用Ramberg-Osgood模型描述[2]，随后的试验发现，在应力和应变较小时，该模型能够比较准确的描述不锈钢的应力应变曲线，在应力应变均较大时，该模型描述的应力会明显大于试验结果，之后提出的修正Ramberg-Osgood[3]模型分两段描述不锈钢的应力应变关系，成功解决了这一难题；其次，不锈钢的应力应变曲线没有明显的屈服点和屈服平台，通常取0.2%的塑性应变对应的应力为名义屈服应力，因此，不锈钢具有更好的冷加工强化性能，常温下，不锈钢与碳素钢的应力应变关系比较如图1所示；再次，不锈钢还表现出一定的各向异性和拉压不对称性。物理性能方面：在不锈钢中的Cr元素含量在12%~18%之间时，表现出良好的耐腐蚀性能。不锈钢的比热容与碳素钢比热容类似，不同的是碳素钢在大约723℃的时候材料发生转化，需要大量吸热，而不锈钢无此现象。不锈钢导热率随温度的升高而增大，与普通碳素钢相反，在1000℃以下时，其导热率均小于普通碳素钢。不锈钢的热膨胀系数比普通碳素钢高约50%，因此在高温条件下，不锈钢会产生更大的热膨胀变形，在约束构件中会产生更大的温度内力[4]。 图1 不锈钢与碳素钢的应力应变关系 早在上世纪20年代，不锈钢就开始作为屋面材料和室内装饰面材料应用到建筑结构中。1925年，在伦敦的圣保罗大教堂的加固工程当中采用了不锈钢拉索，这是不锈钢第一次作为结构承重材料应用到土木工程结构中[5]。然而由于其冶炼需要大量添加Cr、Ni、Mn、Mo等合金元素，使得不锈钢的生产成本长期居高不下，这也大大限制了它在土木工程结构中的应用[5]。直到1968年在美国的圣路易斯大桥拱门中才又一次将不锈钢作为结构材料应用到土木工程结构中。近三十年来，美国、欧盟[6]、日本[7]等一系列发达国家相继出台了不锈钢的设计规范，这才使得不锈钢在土木工程结构中的应用有了较大发展。国内关于不锈钢的研究起步较晚，相关的设计规程还在制定中，不锈钢的应用还主要于用于装饰和网架等次要结构中。 相对于不锈钢在常温下的受力性能和设计方法等方面的进展，不锈钢在高温下的受力性能在近几年才逐渐引起国内外研究人员的重视。本文将对不锈钢的在高温下的受力性能进行总结回顾，包括温度对不锈钢的物理力学性能影响以及高温下的应力应变关系曲线，指出了目前研究中存在的一些问题，展望了未来的研究方向。 1. 高温下的力学性能 1.1 试验研究