毛竹杉木层积复合材的弯曲与剪切破坏过程-国际竹藤中心.docVIP

中国·昆明：2007年6月2日~4日 中国林学会木材科学分会第十一次学术研讨会论文集 毛竹/杉木层积复合材的弯曲与剪切破坏过程 王戈1 江泽慧1 于文吉2 (1.国际竹藤网络中心, 北京 100102; 中国林业科学研究院, 北京 100091) 摘 要：本文利用扫描电镜在位拉伸方法（ISL-SEM），研究了毛竹杉木层积复合材在受到外力作用下三点弯曲和剪切微观破坏过程；结合扫描电镜所观测的形貌图,分析了该情况下层积材的典型破坏规律；并总结了不同气干和水湿处理条件下，竹杉层积复合材弯曲和剪切的破坏模式。 关键词：毛竹杉木层积材　扫描电镜在位拉伸　弯曲　剪切　破坏模式 The bending and shear failure process of Moso bamboo/Chinese fir laminated composite WANG-Ge1 JIANG-Zehui1 YU-Wenji2 (1.International Center for Bamboo and Rattan, Beijing 100102; Chinese Academy of Forestry, Beijing 100091) Abstract： Through in-situ linear-scan electron microscope method (ISL-SEM), the micro-failure process of three-point bending and shearing strength on Moso bamboo/Chinese fir laminated composite under loading had been investigated. On the basis of the images observed by scanning electron microscope(SEM), the typical failure discipline were analyzed. After air-dry condition and water soaking treatment, the failure pattern of bending and shearing strength for Moso bamboo/Chinese fir laminated composite were also summarized in the paper. Keywords： Bamboo/Chinese fir laminated composite, In-situ linear-scan electron microscope, Bending, Shearing, failure mode 复合材料的破坏行为是一种动态的过程，它可能是某一种变化或破坏形式先发生，也可能几种破坏形式同时发生。国内外对破坏后的木材或竹材状态已做过大量的研究，但对动态的破坏过程研究相对很少[1-10]。利用扫描电镜在位拉伸方法可以对固体材料受力时的微区变形、破坏演化过程进行跟踪观察,为描述材料的形变、裂纹扩展和界面破坏规律提供了一种非常有用的手段。本文利用此方法研究毛竹与杉木层积复合材破坏时的动态变化过程，以直观图像的形式观察在施加外力的情况下，竹杉层积复合材弯曲和剪切破坏微观形貌，了解破坏发生的薄弱位置，为有针对性的改进层积材制造工艺提供依据。 1 材料与方法 1.1 材料采集和试样加工 第一作者简介：王戈，1965年生，男，国际竹藤网络中心，副研究员，博士。主要从事木（竹）材料加工与利用。 电话：010电子邮件： HYPERLINK mailto:liqinghzhong@ wangge@。 资助项目：国家林业局948引进项目（2003 – 4 – 27） 毛竹（Phyllostachys pubescens Mazel ex H.de Lebaie）采自浙江省杭州萧山地区，5年生，取去除竹青和竹黄的精刨竹条。杉木（Cunninghamia lanceolata（Lamb.）Hook.）采自湖南省汉寿县军山铺乡的人工林，树龄为14年，取弦向边材，四面刨光加工成杉木条。胶粘剂采用双组分聚异氰酸酯乳液型胶粘剂（简称EPI胶）, 购自太尔公司，型号为DYNOLINK-8000G。 试验用两种毛竹和杉木层积复合结构：（1）将毛竹条和杉木条分别加工成1mm厚的薄条，选取上下表层为毛竹，芯层为杉木的层积复合形式进行胶合（简称BFB型），制成名义规格为30mm（长）