注塑7大因素】（The injection of 7 factors]）.docVIP

注塑7大因素】（The injection of 7 factors]） (time: 2009-5-13 13:15:01 a total of 1547 visits) A, shrinkage The following factors affecting thermoplastic molding shrinkage: 1.1 varieties of plastic thermoplastic plastic molding process because of the presence of the crystalline volume changes shape, inner stress, frozen in plastic residual stress in the large, strong molecular orientation and other factors, so compared with thermosetting plastic shrinkage shrinkage is large, wide range, obvious direction, also forming after the contraction, annealing or conditioning after shrinkage generally than thermosetting plastic. 1.2 pieces of plastic forming properties of molten material and outer cavity surface contact immediately cooled to form solid shell with low density. Due to the poor thermal conductivity of plastic, plastic inner layer of slow cooling and the formation of high density solid layer of large shrinkage. So the wall thickness, slow cooling, high density layer thickness is shrinkage. In addition, there is no insert and insert layout and quantity have a direct impact on the direction of flow, density and shrinkage resistance size, so the shrinkage characteristics of plastic parts of the size and direction of influence. The 1.3 inlet form, size and distribution of these factors directly affect the direction of flow, density, pressure and molding time feeding effect. Direct inlet, inlet section (especially thick section) is small but the direction of contraction, the inlet width and short length direction of small. From the feed port near or with the direction of flow is parallel to the contraction. 1.4 mold molding conditions of high temperature, melt cooling is slow, high density, high shrinkage, especially for crystalline material with high crystallinity and large volume changes, so the greater shrinkage. Mold temperature distribution and plastic parts is also related to internal and external cooling and density uniformity, directly affects the size and direction o