真空紫外线对聚合物材料表面的影响 - 中国电机工程学报.pdf

6 / 2002 8 Influence of VUV Irradiation on the Surface of Polymers 1 1 1 2 1 , , , , ( 1, 150001; 2 , 730000) 1 1 1 2 1 P NG Gui-rong , YANG De-zhuang , H Shi-yu , LI Dan-ming , JIANG Ll-xiang ( 1Space Materials nvironment ngineering Lab. , Harbin Institute of Technology, Harbin 150001, China; 2 National Key Lab of Vacuum Cryogenics. T echnology and Physics Lanzhou, 730000, China) : , ( PTF ) (P T) (VUV) , X (XPS) : ; ; ; : V255.2: A: 1001-4381 ( 2002) 08-0006-04 Abstract : For the widely use of polymers in aerospace, the surface change of polytetrafluoroethylene (PTF ) and poly (ethylene terephthalate) (P T ) in the vacuum ultraviolet (VUV) radiation was investigated. It was shown that PT F and P T turned to dark brown under the VUV radiation in gas-jet VUV simulator. Carbon enrichment was detected for PT F and P T after VUV radiation by XPS. Weight loss of both samples of PTF and P T increased. Key words: vacuum ultraviolet (VUV) ; P T , ; PTF ; gas-jet VUV simulator , - 4 - 5 10 10 , 20 , Pa K , , , , [ 1, 2] X , , , , , , 300nm : 506625 , , Pa