如何应对现浇住宅楼板产生裂缝.docVIP

如何应对现浇住宅楼板产生裂缝摘要：如某市一住宅小区有四栋高层,该工程经实地查看发现房屋均存在宽度0.2mm-0.4mm的裂缝,位置多处在板四周阳角处。根据业主要求组织有关单位复查，发现房屋沉降量、倾斜度、混凝土强度都满足设计要求，各种原材料均合格。施工图纸也符合有关规范要求。鉴于上述情况,经过认真分析,确认引起现浇板裂缝原因有以下几点。 关键词：框剪结构;裂缝;住宅楼板 Abstract: As a city, a residential district with four high-level of the project through field visits to the houses there are a width of 0.2mm-0.4mm cracks, the location of many around in the board Yang corner. Review of the relevant units of housing settlement, inclination, concrete strength to meet design requirements, a variety of raw materials are qualified according to the requirements of owners. Construction drawings comply with the relevant regulatory requirements. After careful analysis, this paper to confirm the following reasons of caused Slab cracks.Key words: frame structure; cracks; residential floor 中图分类号： TV543+.6 文献标识码：A文章编号：2095-2104（2012） (一)板负筋下沉产生的裂缝:在楼面工程施工中各种交叉作业,楼面负筋位置的正确性难以得到保证,由于受到施工人员踩踏后会使钢筋弯曲、变形,致使负筋下陷,保护层过大,降低了板截面的有效高度,使板的承载能力达不到设计的要求,从而导致板裂缝的产生。 （二）混凝土的收缩:混凝土的收缩变形是混凝土的固有特性,主要表现形式为浇筑初期(终凝前)的凝缩变形、硬化过程中的干缩变形、在恒温绝湿条件下由凝胶材料的水化作用引起的自身收缩变形和温度下降引起的冷缩变形。 1、终凝前的凝缩变形 凝缩变形产生的裂缝发生在混凝土结硬前最初几小时内,通常浇筑后24h即可观察到。这种裂缝有两类:一类是由于塑性混凝土下沉产生的裂缝,在梁、板中都有可能产生;另一类是塑性收缩裂缝,常出现在板中,裂缝逞不规则的鸡爪状或地图状。凝缩变形产生的裂缝多与混凝土的泌水现象有关。 新浇筑的混凝土经压实后,由于重力作用,重的固体颗粒向下沉,迫使轻的水向上移,即所谓“泌水”。当固体颗粒彼此支撑不再下沉,或水泥结硬阻碍了它的下沉,泌水即停止。如混凝土中固体颗粒能不受阻碍地自由下沉,则仅使结硬后混凝土的体积减少,并不会产生裂缝。 2、硬化过程中的干缩和水化作用引起的自身收缩 自身收缩与干缩一样,在浇筑后相当长的时间,约1～2d才会出现,它是由于水的迁移而引起的。但它不是由于水向外蒸发散失,而是因为水泥水化时消耗水分造成凝胶孔的液面下降,形成弯月面,产生所谓自干燥作用,使混凝土体的相对湿度降低和体积减少;水灰比的变化对干燥收缩和自身收缩的影响正相反,即当混凝土的水灰比降低时干燥收缩减少,而自身收缩增大。 3、温度下降引起的冷缩变形 收缩裂缝由温度影响产生的另一种裂缝,是混凝土外约束引起的,大多发生在混凝土的降温阶段,混凝土逐渐散热和冷却收缩过程中,全部或部分外约束,会产生较大的拉应力,当拉应力超过混凝土极限抗拉强度,就会产生降温收缩裂缝,收缩裂缝多在混凝土养护一段时间才出现的,裂缝较深,有时是贯通性的。 二、防治措施 现浇板结构设计中除考虑强度要求外,还应进行挠度及裂缝验算,考虑施工不均匀性及混凝土本身的收缩因素,适当增加板厚,增强板的刚度。应在楼板上每隔20m左右处设置一后浇带,并在楼板中间墙体支座处设一条伸缩缝,使其释放内应力。楼板因四周嵌固于墙体内,应在四角部位按要求配置双向钢筋,伸出长度应小于1/3L(L 为短向边长),且不小于1.2m为宜。在抗震非设防地区,也应适当增设混凝土构造柱,提高房屋整体抗震强度。 施工方面应严格按配合比进行计量投料,控制搅拌时间及水灰比,并根据现场砂含水量变化及原砂中含粒径5cm以上的砾石筛选调整施