二氧化碳保护焊接规范和操作工艺作业指导书（Carbon dioxide arc welding specification and process work instructions）.docVIP

二氧化碳保护焊接规范和操作工艺作业指导书（Carbon dioxide arc welding specification and process work instructions） Carbon dioxide protection welding specification and operation process operation instruction 2009-08-30 CO 2 gas for CO2 gas shielded welding, most of which is an industrial by-product, which is compressed into Liquid bottling. At normal temperature, when the standard bottle is full, the pressure is from 5 to 7MPa (5 O to 7 Okgf / cm2). Less than 1 MPa (10 table pressure), can not continue to use. C02 gas for welding, general technology The purity required by the standard is more than 99%. If it is found to be of low purity, it should be purified. When welding low carbon steel and low alloy steel, carbon dioxide welding is used to ensure high weld seam The mechanical properties and the prevention of porosity must be made of alloy steel wires containing manganese, silicon and other deoxidizing elements The carbon content in the welding wire shall be limited. Among them, H08Mn 2SiA is used more widely, mainly used for low carbon steel and low alloy steel H 04Mn 2SiTiA contains very low carbon content, and contains 0.2% to 0.4% titanium elements, anti gas With high porosity, it is used on weld seams with high compactness. The specifications of CO2 gas shielded arc welding include power polarity, wire diameter, arc voltage and welding Current, gas flow rate, welding speed, wire extension length, DC loop inductance, etc.. (1) when the power polarity carbon dioxide gas shielded welding is used for welding general materials, the direct current reverse connection is adopted; DC welding shall be adopted for high speed welding, surfacing welding and cast iron repair welding. (two) the diameter of welding wire diameter of carbon dioxide gas shielded arc welding can be chosen according to table. (three) arc voltage and welding current are protective of carbon dioxide gas for welding wire of a certain diameter In welding, a lower arc voltage and a smaller welding current are used to fuse