混凝土产生裂缝原因及控制措施.docVIP

混凝土产生裂缝原因及控制措施摘要：分析了混凝土裂缝产生的原因，为了保证现浇混凝土效果和耐久性，除了正确合理的设计以外，必须严格提高施工技术水平，裂缝的出现不但会影响结构的整体性和刚度，还会引起钢筋的镑蚀、加速混凝土的碳化、降低混凝土的耐久性和抗疲劳、抗渗能力。因此根据裂缝的性质和具体情况我们要区别对待、及时处理，以保证建筑物的安全使用。 关键词：混凝土;现浇;裂缝;质量;控制措施 Abstract: the author analyzes the cause of concrete crack, in order to guarantee cast-in-situ concrete effect and durability, besides right outside the reasonable design, must be strictly improve the construction technology level, the occurrence of crack will not only affect the structure of integrity and stiffness, can also cause corrosion of reinforcement concrete, accelerating the pound carbide, reduce the durability of concrete and resist fatigue, anti-permeability ability. Therefore according to the nature of the cracks and circumstances we should be kept separate, handled in a timely manner, to ensure the safe use of the building. Keywords: concrete; The site; Crack; Quality; Control measures 中图分类号： TU528 文献标识码：A 文章编号： 混凝土施工过程中，裂缝的产生不可能完全避免，只要裂缝的数量、形状及发展趋势不会影响建筑物的受力及表面感观，就可以不进行处理。如果裂缝的发展有可能对建筑物的整体受力造成严重影响，或建筑物表面裂缝影响了人们的感观舒适度，给人造成危险感，那就有必要对裂缝进行控制和治理。目前，不同规范对建筑物所要求的耐久性、美观度不同，对需要处理的裂缝规定也有所不同。以下从几方面对混凝土裂缝产生的原因和防治措施进行论述，供技术人员参考。 1、大体积混凝土产生裂缝的主要原因 1.1水泥水化热 水泥在水化过程中要释放出一定的热量，而大体积混凝土结构断面较厚，表面系数相对较小，所以水泥发生的热量聚集在结构内部不易散失。这样混凝土内部的水化热无法及时散发出去，以至于越积越高，使内外温差增大。单位时间混凝土释放的水泥水化热，与混凝土单位体积中水泥用量和水泥品种有关，并随混凝土的龄期而增长。由于混凝土结构表面可以自然散热，实际上内部的最高温度，多数发生在浇筑后的最初3～5天。 1.2外界气温变化 大体积混凝土在施工阶段，它的浇筑温度随着外界气温变化而变化。特别是气温骤降，会大大增加内外层混凝土温差。应采取温度控制措施，防止混凝土内外温差引起的温度应力。 1.3混凝土的收缩 混凝土收缩的主要原因是内部水蒸发引起混凝土收缩。干湿交替会引起混凝土体积的交替变化，这对混凝土是很不利的。 2、混凝土裂缝裂缝处理措施 混凝土裂缝的修补措施主要有以下一些方法：表面修补法，灌浆、嵌逢封堵法，结构加固法。混凝土置换法，电化学防护法以及仿生自愈合法。 2.1表面修补法 表面修补法是一种简单、常见的修补方法，它主要适用于稳定和对结构承载能力没有影响的表面裂缝以及深进裂缝的处理。通常的处理措施是在裂缝的表面涂抹水泥浆、环氧胶泥或在混凝土表面涂刷油漆、沥青等防腐材料，在防护的同时为了防止混凝土受各种作用的影响继续开裂，通常可以采用在裂缝的表面粘贴玻璃纤维布等措施。 2.2灌浆、嵌逢封堵法 灌浆法主要适用于对结构整体性有影响或有防渗要求的混凝土裂缝的修补，它是利用压力设备将胶结材料压人混凝土的裂缝中，胶结材料硬化后与混凝土形成一个整体，从而起到封堵加固的目的，常用的胶结材料有水泥浆、环氧树脂、甲基丙烯酸酯、聚氨酯等化学材料。 嵌缝法是裂缝封堵中最常用的一种方法，它通常是沿裂缝凿槽，在槽中嵌填塑性或刚性止水材料，以达到封闭裂缝的目的。常用的塑性材料有聚氯乙烯胶