窑系统各部位耐火衬料设计及应用（Design and application of refractory lining for each part of kiln system）.docVIP

窑系统各部位耐火衬料设计及应用（Design and application of refractory lining for each part of kiln system） Refractory in large pre decomposition. Due to the thermal load increases, all should be intensified and corrosion. The working environment is very bad, so the refractory lining to strict selection and matching A kiln discharge port and discharge belt Effect of lining the hot two air and flame radiation material by hot alkali clinker, carry dust and the two places of the mechanical wear and chemical erosion are very serious. Therefore, the requirements for these parts of the lining has good abrasion resistance and resistance to temperature shock property. Unloading belt generally use the AI2O3 content of 80-90% high aluminum brick, thermal shock resistance of high alumina brick, magnesia spinel brick and magnesia chrome brick; discharge port using high alumina brick and corundum as heat-resistant concrete aggregate, sometimes the use of silicon carbide. Two, the burning zone The burning zone lining the main shock under high temperature and chemical erosion, especially the heat load of large kiln increased, exacerbated by the destruction of their role. Therefore, the refractory material sintering belt use, in addition to the requirements of fire out enough, also easy to stick to the kiln lining protection at high temperature. At present, firing with alkaline refractory materials such as magnesium and chromium in common use, thermal expansion coefficient, elasticity is poor, if not because of the brick kiln skin protection, temperature stress is too large, easy to break off. Generally speaking, the higher content of C2F and C2S in brick, brick and favor between clinker reaction with iron, magnesium mud or steel material as a gap lined lining material to help skin sticking kiln. At the same time, in order to obtain lining material and kiln crust sticking between dense stomata alkaline brick rate should not be too small to 16-20% is more appropriate. The burning zone lining material