试析建筑工程混凝土裂缝成因及防范对策.docVIP

试析建筑工程混凝土裂缝成因及防范对策摘要：建筑工程混凝土的裂缝问题是一个普遍存在而又难以解决的工程问题，混凝土裂缝的存在和发展通常会使内部的钢筋等材料产生腐蚀，降低钢筋混凝土材料的承载能力、耐久性及抗渗能力，影响建筑物的外观、使用寿命，严重的将威胁到人民的生命、财产安全，如何在施工中有效控制裂缝的产生，本文将混凝土裂缝问题进行了归纳、分析并针对具体情况提出了一些预防、处理措施。 关键词：混凝土；裂缝；成因；措施 Abstract: the construction of concrete crack problem is a widespread and it is difficult to solve engineering problems, the concrete cracks the existence and the development of internal will usually reinforced materials such as corrosive, reduce the carrying capacity of reinforced concrete materials, the durability and anti-permeability ability, affect the appearance of the building, service life and serious threat to people’s life and property safety, how to effectively control in the construction of the cracks of, this article will concrete crack problems on the comprehensive analysis and in the light of specific conditions puts forward some prevention and treatment measures. Keywords: concrete; Crack; Cause; measures 中图分类号：TU37文献标识码：A 文章编号： 建筑工程生产中，倘若混凝土构件出现裂缝，就有可能影响到混凝土构件的刚度和建筑物结构的整体抵抗能力，影响结构构件的耐久性能。因此，对混凝土裂缝问题，要给与高度重视，准确把握裂缝产生、发展的根本原因，并从设计施工上采取相应的措施，预防并控制裂缝的发生、发展。 一、裂缝的原因分析 由于混凝土的组成材料、微观构造以及所受外界影响的不同，混凝土中产生裂缝有多种原因，主要是温度和湿度的变化，混凝土的脆性和不均匀性，以及结构不合理，原材料不合格，模板变形，基础不均匀沉降等。 （1）材料的原因 混凝土加水拌和后，水泥中的碱性物质与活性骨料中活性氧化硅等起反应，析出的胶状碱——硅胶从周围介质中吸水膨涨，体积增大三倍，从而使混凝土涨裂产生裂缝。另外，粗细集料含泥量过大，造成混凝土收缩增大。集料颗粒级配不良或采取不恰当的间断级配，容易造成沪宁图收缩的增大，诱导裂缝的产生。由于原材料质地不均匀、水灰比不稳定以及运输和浇筑过程中的离析现象，在同一块体混凝土中其抗拉强度也是不均匀的，存在着许多抗拉能力很低，易于出现裂缝的薄弱部位。 （2）温差的原因 混凝土在硬化期间水泥产生大量水化热，内部温度不断上升，在混凝土表面引起拉应力。后期在降温过程中，由于受到基础或老混凝土的约束，又会在混凝土内部出现拉应力。气温的降低也会在混凝土表面引起很大的拉应力，当这些拉应力超出混凝土的抗裂能力时，即会出现裂缝。当有约束时，混凝土热涨冷缩所产生的体积涨缩，因为受到约束力的限制，在内部产生了温度应力，由于混凝土抗拉强度较低，容易被温度引起的拉应力拉裂，从而产生温度裂缝。由于太阳暴晒产生裂缝也是工程中最常见的现象。 （3）干缩及负荷过重的原因 许多混凝土的内部湿度变化很小或变化较慢，但表面湿度可能变化较大或发生剧烈变化，如养护不当、时干时湿，表面干缩变形受到内部混凝土体的约束，也往往产生裂缝。构件超载产生的裂缝，例如：构件在超出设计的均布荷载或集中荷载作用下产生内力弯矩，出现垂直于构件纵轴的裂缝，构件在较大剪力作用下，产生斜裂缝，并向上、下延伸。 （4）周围环境的原因 当钢筋混凝土处于不利环境中，例如：侵蚀性水，由于混凝土保护层厚度有限，特别是当混凝土密实性不良，环境中的氯离子等和溶于水中的氧会使混凝土中的钢筋生锈，生成氧化铁，氧化铁的体积比原来金属的体积大的多，铁锈体积膨胀，对周围混凝土挤压，使