SP1500具体参数及使用注意事项.docVIP

Himilan? SP1500 Purge compound resin For Extrusion Coating Product Information  Description Himilan? SP1500 is a purge compound resin designed to use after processing of Ionomer and/or acid copolymer in conventional extrusion and co-extrusion coating equipment. Features/Benefits ? Excellent purge efficiency to purge out Ionomer and/or acid copolymer, especially at the dead space in adapter and/or die ? Easily switched from SP1500 to PE ? Shorten purge time compared to PE purge ? Much less fume and odor compared to conventional purge compounds Table 1 Properties of Himilan? SP1500  Resin Property Typical Value Test Method Melt Flow Index, dg/min 0.8 ASTM D1238 Cond. 190°C/2.16 kg Density, g/cc 1.051 ASTM D792 Vicat Soft Point, 87 ASTM D1525 Processing Information A typical procedure for use of Himilan? SP1500 is shown in Figure 1. Actual purge procedure will usually be determined by either the specific equipment or the type of Ionomer and/or acid copolymer. Figure 1. Typical procedure (Ionomer/Acid copolymer to LDPE) for 90mmExtruder Resin Quantity Temp. profile Notes Ionomer/Acid copolymer Production C1 : 180 C2 : 260 C3D : 290-300 Advisable; - Screw Cooling - Cooling at bottom of Hopper SP1500 Purge start 25kg C1 : 200 C2 : 280 C3D : 320 1.Temperature profile will be changed when SP1500 is put into Extruder 2.Move deckle outside and remove rod 3.Raise screw speed so far as maximum motor load and resin pressure 4.When SP1500 comes out across the die, reduce screw speed minimum, like 10rpm 5.Raise screw speed again after temperature is reached at the designed profile Pay attention to motor load and resin pressure LDPE (MI=3- 4g/10min) 50kg C1 : 200 C2 : 280 C3D : 320 1.Never leave SP1500 in hopper 2.LDPE will run after melt web is completely clear 3.Often move deckle in and out However, close to the end of purge, move deckle out and  fix it 4.Change temp. profile suitable for next production after purge is completed LDPE (or other resins)