水性涂料用丙烯酸树脂的制备缩写稿遗书doc.docVIP

水性涂料用丙烯酸树脂的制备 化工104班：唐春花 指导教师:唐宏科 （陕西科技大学化学与化工学院 陕西 西安 710021） 摘要：本文以甲基丙烯酸甲酯（MMA)、丙烯酸丁酯(BA)和丙烯酸(AA)为单体，以正丁醇为溶剂，过氧化苯甲酰(BPO)为热引发剂，制得了水性丙烯酸树脂。着重讨论反应温度、时间，单体、引发剂和中和剂用量对水性丙烯酸树脂性能的影响。结果表明，合成水性丙烯酸树脂的最佳工艺条件为：丙烯酸AA为单体总摩尔质量的12.5%，甲基丙烯酸甲酯(MMA)：丙烯酸丁酯（BA)为1:1，引发剂用量为单体总摩尔质量的0.5%，反应温度为100℃，反应时间为3h，中和度为90%。ABSTRACT:In this paper, with methyl methacrylate (MMA), butyl acrylate (BA) and acrylic acid (AA) as the monomer, with n-butyl alcohol as the solvent and benzoyl peroxide (BPO) as the thermal initiator, with water-based acrylic resin.Focuses on reaction temperature, time, dosage of monomer, initiator, and neutralizing agent on the properties of water-based acrylic resin.The results showed that the optimum condition for synthesis of water-based acrylic resin for:Acrylic AA 12.5% of the total molar mass of monomer, methyl methacrylate (MMA), butyl acrylate (BA) as 1:1, initiator dosage is 0.5% of the total molar mass of monomer, reaction temperature is 100 ℃, reaction time is 3 h, neutralization degree of 90%.KEY WORDS: acrylic resin，monomer ，coating，solution polymerization 1 概述 水性丙烯酸树脂的溶液聚合是指把单体和引发剂溶解在适当的溶剂中进行的聚合反应。在聚合反应中,溶剂起了稀释剂的作用,所以溶液聚合的体系粘度较低,物料混合和传热都比较容易,凝胶效应不易出现,反应温度容易控制,同时也有利于散热。本文选用了硬单体甲基丙烯酸甲酯（MMA）、软单体丙烯酸丁酯（BA）、功能单体丙烯酸（AA）制备的丙烯酸树脂具有优良的耐候、耐化学品性,优良的保色性和附着力,具有高光泽和持久性。 22.1实验药品 丙烯酸丁酯（BA） 甲基丙烯酸甲酯 (MMA) 丙烯酸（AA）氨水 过氧化苯甲酰（BPO） 正丁醇 3 结果与讨论 3.1不同单体用量对树脂性能的影响 3.1.1 AA用量对丙烯酸树脂性能的影响 3-1-1 AA含量对溶液透光率的影响 AA%较低时水溶性就差，树脂黏度随AA用量的增加而增大，而AA%过高有会影响共聚物膜的耐水性,同时中和成盐的黏度也较大，综合考虑，选用AA在单体中的含量为12.5%比较合适。 3.1.2 随引发剂BPO用量的增加，树脂的转化率增加，黏度降低。当引发剂用量为单体总量的0.5%时，转化率都在90%以上。用量更高时，转化率和黏度都趋于平缓。%. 3.2反应温度对树脂性能的影响 3-2-1 反应温度对树脂转化率的影响 3-2-2 反应温度对树脂黏度的影响 随反应温度的增加，树脂的转化率增大，黏度无多大变化。 当温度达到100℃左右时，树脂转化率最大，随着温度的再升高，树脂转化率降低。 3.3 反应时间对树脂性能的影响 3-3-1 反应时间对树脂转化率的影响 3-3-2 反应时间对树脂黏度的影响 随着反应时间的延长，树脂的转化率略有增大，黏度基本没有变化。但反应时间过长，会延长聚合反应时间,反应体系在高温下会发生其它副反应,影响产品的树脂和转化率的质量。综合考虑，反应时间为3小时比较合适。3.4 中和剂对树脂性能的影响 随着中和度的增加，树脂黏度和溶液透光率增大。但是黏度太大，不利于涂料的制备， 即使在使用树脂时可通过加水来稀释黏度，也会降低