铝合金状态代号（Aluminum alloy status code）.docVIP

铝合金状态代号（Aluminum alloy status code） Alloy basic state code: F free machining conditions are applicable to the products which are specially required for working hardening and heat treatment conditions in the forming process, and the mechanical properties of this state product are not specified (not very common) O annealed conditions are applicable to annealed products with minimum strength (occasionally) H hardening condition applied to improve the strength of the product through the hardening product in hardening after after (or not after) additional heat treatment. The strength decreased (the general non material heat treatment) W solid fusion heat treatment state is an unstable state which is only applicable to naturally aged alloy at room temperature after solid solution heat treatment. The condition code only indicates that the product is in the natural aging stage (not very common) T heat treatment status (different from F, O, H state), suitable for heat treatment, after (or without) work hardening, to achieve stable products. T code must be followed by one or more Arabia digital (usually heat treatment reinforced material), our common non heat treatment reinforced aluminum alloy behind the status code is usually the letter H plus two digits. Such as 1100 H14. The following brief describes the meaning of the following status code content. The letter H is followed by two digits: the first number indicates the method of work hardening. The first digits behind H are: 1, 2, 3, 4 That is, H1* H1* stands for simple work hardening H2* H2* indicates work hardening and incomplete annealing H3* H3* indicates work hardening and stabilization treatment H4* H4* stands for work hardening and painting treatment The second digit indicates the degree of hardening of the material. The second digits behind H are: 1, 2, 3, 4, 5,, 6, 7, 8, and 9 Hardness between H*1 0 and 2 H*2 1/4 hard Hardness between H*3 2 and 4 Hardness between H*4 1/2 hard H*5 4 and 6 Hardness between H*6 3/4