轴承座设计（Bearing block design）.docVIP

轴承座设计（Bearing block design） According to the process plan, a detailed procedure is worked out as follows: The blank for casting, cleaning, annealing treatment to eliminate internal stress and improve the mechanical properties of castings, to riser in the rough milling workshop, required to achieve the blank of technology, and then sent to the machine shop for processing. Working procedure: 1. the bottom surface of the rough milling base is based on the upper surface of the bearing seat, and the rough material is clamped in the upper surface X6132 universal horizontal milling machine, according to rough margin to rough milling blank. 2., the bottom of the milling base is based on a rough milling machine. According to the actual situation, the relevant parameters of the milling machine are adjusted, and the bottom surface of the bearing seat is carefully machined. 3. roughing milling face 4. roughing top surface 5. bore 62.5 bore 6. drill a hole of 12 mm 7. drill a hole of 16 mm 8. deburring 9. inspection According to the process arrangement, make out the mechanical process card and process card. See Schedule 10: mechanical processing process card; schedule 20~90; machining process card. (three) the allowance of machining, the size of process and the determination of blank size. 1. blank size determination, painting rough figure. The bearing block is HT200. Due to the products low precision requirements, the production program for the middle batch production, so the rough sand casting. The blank is cast to be annealed to eliminate the internal stress in the casting process. By document (1) table 2-2, the dimension tolerance grade of this kind of casting is IT9 grade. From the document (1) table 2-2, the tolerance of the main dimensions of the casting can be found, and the main blank size and tolerances are shown: And... 2. bottom surface of rough milling base The bottom surface by rough milling and finish milling two processing is completed, the three blade circular f