大体积砼外观颜色不均分析及改进措施（Analysis of uneven appearance color of mass concrete and improvement measures）.docVIP

大体积砼外观颜色不均分析及改进措施（Analysis of uneven appearance color of mass concrete and improvement measures） Analysis of uneven appearance color of mass concrete and improvement measures In combination with the construction of a bridge pier, from concrete materials, concrete mix proportion and construction technology of concrete appearance and other reasons are analyzed, put forward the technical measures to prevent the concrete appearance of uneven color, and achieved good results. Keywords concrete color; uneven analysis; improvement measures; 1. overview: In the construction of mass concrete, the phenomenon of uneven appearance of concrete color often occurs, seriously affecting the appearance quality of concrete, and once it appears, there is no way to deal with it. The pier bridge pier, a total of 61, the pier height between 7~30 meters, mostly in the 25 meters above the most concrete at around 250. The concrete strength is C20, raw materials: cement is a cement plant * * brand P.O32.5 cement, coarse aggregate 5~40mm natural fine aggregate is gravel, sand, coarse sand. The concrete mix ratio is C:S:G:W=1:2.41:4.29:0.57, the cement dosage is 290kg/m3, the water cement ratio is 0.57, the sand rate is 36%, and the slump is 5~7cm. At the beginning of the pier concrete tube string into the mold, after the change of concrete directly into the mold in place, the use of plug-in vibrator vibrated, a pouring molding construction process. 33# pier after stripping concrete appearance color uneven, showing deep or shallow phenomenon, and generally layered, deep color part of some less than 1cm in diameter, white spots, seriously affected the appearance quality of pier. Through the analysis of the measures taken to improve, pier construction in the concrete appearance of uniform color, and achieved good results. 2. uneven color causes analysis The concrete appearance of uneven color the most fundamental reason is that in the concrete mixture in the construction process due to the reason