环保型银镀层防变剂研究.pdfVIP

环保型银镀层防变色剂研究 郭国才 上海应用技术学院化学工程系，上海 200235 摘要：本文研发了一种环保型的银镀层防变色剂(FBS)，通过H S气氛暴露实验 2 ，Na S浸渍实验和电化学实验，研究了该防变色剂及与其它缓蚀剂复配时对银 2 镀层的防变色性能，确定了其最佳用量为0.2g/L 。电化学实验表明，该防变色 剂与其它缓蚀剂具有很好的协同效应，缓蚀效率大幅度提高。 关键词：银镀层；防变色；腐蚀速度 中图分类号：TG174.42 文献标识码：A Study on Environmentally Friendly Anti-discoloration Agent for Silver Coating GUO Guo-cai (School of Chemical Engineering, Shanghai Institute of Technology, Shanghai 200235) Abstract: A kind of environmentally friendly anti-discoloration agent(FBS) for sliver coating was developed in this paper. The optimum concentration of FBS was established as 0.2g/L by experiments of H S atmosphere exposition, Na S soak and 2 2 electrochemistry. The electrochemical experiments showed the agent had good synergistic and corrosion inhibition effect with other inhibitors. Keywords: silver coating; anti-discoloration; erosion speed 引言 银镀层具有光亮的银白色、优良的导电、导热及焊接性能；随着电子技术的日 益发展，银镀层广泛应用于计算机、通讯、家用消费类电子产品行业。但是银 镀层极易在大气环境中变色，由闪亮的光泽渐渐地转变为黄色、棕褐色，严重 的影响镀银层的外观；同时镀银层变色使镀银件的焊接性能下降、接触电阻增 加，电能损耗加大，电子设备的稳定性、可靠性下降[1- 2] 。镀银层变色问题已引起国内外学者的格外关注并进行了大量研究。在综合了 国内外有关防变色剂发展和研究的基础上，本文作者研制了一种环保型、水溶 性的镀银层防变色剂FBS，并深入研究了该防变色剂的性能。 1 实验部分 1.1 H S气氛实验 2 实验条件按照GB/*5943- 86轻工产品金属镀层和化学处理的抗变色腐蚀实验方法进行。取一个干净的2.5 L干燥器，在其底部中间放置一个小烧杯，倒入稍微稀释的所需量浓硫酸,然后 盖上干燥器的挡板(上有许多孔) ，将经过防变色剂处理的镀银试样编号后依次 放在挡板上。然后把所需要量的硫化钠加少量蒸馏水溶解后，通过挡板上孔洞 倒入小烧杯中，迅速盖上干燥器盖子，观察现象、记录数据。 1.2 Na S浸渍实验 2 配制浓度为5%的Na S溶液，在室温条件下，将经过防变色剂处理的镀银 2 试样浸入其中，观察表面变色情况并记录变色时间。 1.3 腐蚀速度测试 室温下，在20mg/L 的Na S溶液中，采用动电位扫描法测量FBS 防变色剂及其与 2 协同缓蚀剂在不同浓度下的腐蚀速度及缓蚀效率。实验在三电极体系下进行，