li2co3助烧钴镍共掺batio3基ntc热敏材料-ingentaconnect.pdf

See discussions, stats, and author profiles for this publication at: /publication/263409019 Co/Ni Co-doped BaTiO3 based NTC thermistors with Li2CO3 as sintering additive Article in uei Suan Jen Hsueh Pao/ Journal of the Chinese Ceramic Society · June 2011 CITATIONS READS 0 15 5 authors, including: Zhicheng Li Central South University 76 PUBLICATIONS 632 CITATIONS SEE PROFILE All content following this page was uploaded by Zhicheng Li on 24 February 2016. The user has requested enhancement of the downloaded file. · 978 · 硅 酸 盐 学 报 2011 年 第39 卷第6 期 硅 酸 盐 学 报 Vol. 39 ，No. 6 2 0 1 1 年 6 月 JOURNAL OF THE CHINESE CERAMIC SOCIETY J u n e ，2 0 1 1 Li2CO3 助烧钴镍共掺BaTiO3 基NTC 热敏材料 陈景超，张鸿，李根，汪键，李志成 ( 中南大学材料科学与工程学院，长沙 410083) 摘 要：为了开发新型负温度系数(negative temperature coefficient，NTC)热敏陶瓷材料，采用湿化学法制备钴镍共掺BaTiO (BaTi Ni Co O ，x = 3 0.9–x 0.1 x 3–δ 0.05，0.08，0.10，摩尔分数)粉体，并以质量分数为0.5% 的 Li CO 为助烧剂，用传统烧结工艺制备相关陶瓷。用X 射线衍射和扫描电子显微镜分析 2 3 陶瓷的相组成与微观结构，用电阻–温度特性测试和交流阻抗谱分析研究BaTi Ni Co O 陶瓷的电学性能。结果表明：在1 373 K 烧结可以获得致 0.9–x 0.1 x 3–δ 密性好的陶瓷样品；该材料体系具有六方系晶体结构并呈现明显的NTC 效应；x = 0.05、0.08、0.10 样品的材料常数B 分别为3 590、3 796、3 354 K 。 用电子跃迁机理分析材料的NTC 导电特性。 关键词：钛酸钡；钴镍共掺；相组成；导电性；负温度系数