矿粉试验（Slag test）.doc

矿粉试验（Slag test） Test method for mineral powder According to GB/T 176, the ignition temperature of the ignition loss is 700 DEG C + 50 DEG C, the heating time is 15min per time, and the burning time is measured. Weigh about 1g sample, accurate to 0.0001g, have been measured in a porcelain crucible burning, the cover is obliquely arranged in the crucible, put in the muffle furnace in low temperature gradually increased from the temperature at 650 to 750 DEG C under the burning of 15 ~ 20min, took place in the dryer crucible cooling to room temperature, weighing. Repeated burning, until constant. Mass percentage of burn loss = = (quality of sample - quality of sample after burning) / sample quality * 100% Loss of ignition (%) S= (G1-G2) /G1*100 G1 quality before burning and quality after G2 burning Test method of fly ash First, the fly ash is dried to a constant weight (105 DEG C); Take a dry crucible and weigh m1; Weighing about 1.0000g of fly ash material by analytical balance, the actual weight is m2; Into the muffle furnace or electric furnace, began to heat up, 850-900 in constant temperature 15-20min; Take out and place in a desiccator until it is cooled to room temperature. Weigh the crucible and weigh the material m3; Calculation method of ignition loss: (m1+m2-m3) /m2 * 100% C50 or less, less than or equal to 3 / C50 below 5 Its not that complicated. The main use of fly ash is to be used as concrete admixture. In fact, the amount of carbon loss is characterized by carbon content, carbon intensity of the concrete is very large, of course, the smaller the better. There is a relation between the amount of burning loss and the amount of admixture and the slump loss of concrete The smaller the burn loss, the better the effect. Specification for fly ash cement! Aerated concrete equipment, fly ash to provide siliceous materials and calcium material reaction, the formation of hydration products, contribute to the strength of the product. The fly ash can also be used a