胶衣的喷涂和涂刷（The spraying and brushing coating）.docVIP

胶衣的喷涂和涂刷（The spraying and brushing coating） A gel coat, spraying and brushing In order to improve and beautify the surface state of glass steel products, improve product value, and the inner glass steel from erosion, prolong the service life of products, we will generally work surface products into a layer with pigment paste (paste), high content of resin adhesive, it is also pure resin. Available surface mat reinforced. The adhesive layer is called gel coat (also known as the surface layer or decorative layer). Production quality of gel coat will directly affect the product quality and the external resistance, water resistance and chemical resistance of erosion, so in the gel coat spraying or brushing should pay attention to the following points: (1) the configuration of gel coat resin, to fully mix, especially the use of pigment paste, if uneven mixing, will make the products appear on the surface of spots and stripes, which not only affects the appearance, but also reduce its physical properties. This should be possible by mechanical stirring and mixing, the best mixing machine does not produce a whirlpool, to avoid entering into the air. (2) gel can brush or spray gun to spray. When spraying should be volatilization viscosity and added spraying process adding 5~7% styrene resin of styrene to adjust. (3) coating layer thickness should be accurately controlled at 0.3~O.5mm, usually in the unit area are used to control the quality of gel, the gel dosage is 350~550g/ square meters, so that they can achieve the required thickness. Gel coat thickness should be appropriate, not too thin, but not too thick, if the coat is too thin, may be curing incomplete, and gel on the back of the glass fiber easily exposed, affecting the appearance quality, not to beautify and protect glass steel products; if the coat is too thick, it is easy to crack. Not resistant to impact, especially not stand from the opposite direction to the impact of products. Coat brushing is not uniform in