奥氏体不锈钢制容器典型失效案例分析.PDFVIP

奥氏体不锈钢制容器典型失效案例分析 姜海一 贾国栋 王辉 谢国山 史进 陈彦泽 杜晨阳 魏文涛 （中国特种设备检测研究院，北京，100013） 摘 要：本文通过近几年开展的奥氏体不锈钢制容器的氯化物应力腐蚀、腐蚀疲劳和结构失稳的失效分析实 例，综合运用多种计算、检测、试验手段对奥氏体不锈钢制容器的典型失效事故进行分析，并提出失效事故 的预防对策，本文所采用的失效分析方法对奥氏体不锈钢制容器的失效分析工作具有一定的借鉴意义。 关键词：奥氏体不锈钢制容器 ；失效分析 ；预防对策 ；氯化物应力腐蚀 ；腐蚀疲劳 ；结构失稳 Typical Failure Cases of Austenitic Stainless Steel Vessels Jiang Hai-yi Jia Guo-dong Wang Hui Xie Guo-shan Shi Jin Chen Yan-ze Du Chen-yang Wei Wen-tao （China Special Equipment Inspection and Research Institute，Beijing ，100013） Abstract: According to some failure cases of austenitic stainless steel vessels ’ chloride stress corrosion, corrosion fatigue and structure buckling which had been analyzed in recent years, kinds of calculation, inspection and test methods had been multi-applied to analyze these typical failure cases. And some suggestions to avoid these failures have been offered at the last. The failure analysis method mentioned in this article can be helpful to the analysis works of austenitic stainless steel vessels’failure. Keywords: austenitic stainless steel vessel；failure analysis ；prevention method ；chloride stress corrosion ；corrosion fatigue；structure buckling 1 概述 国内外对制造容器用材在不同腐蚀工况下的适用性研究已进行了许多工作。随着石油化 工装备长周期安全运行的迫切需要以及在线检测技术的不断进步，关于石油化工装备的预测 剩余寿命、确定检验周期和报废期方面的腐蚀机理和防腐应用研究也得到进一步发展。 奥氏体不锈钢因其具有良好的耐蚀性和可焊性而广泛地应用于核电设备、蒸汽发电厂和 石油化工行业。但国内对奥氏体不锈钢的应用还不够成熟，奥氏体不锈钢容器的失效事故不 断重复地发生，有必要对奥氏体不锈钢容器的典型失效事故进行分析。 奥氏体不锈钢的失效模式主要有晶间腐蚀、应力腐蚀、腐蚀疲劳和结构失稳。 晶间腐蚀是奥氏体不锈钢（尤其是其焊缝）最早发现的一种典型失效模式。在焊接过程 中，由于焊缝长期停留在敏化温度下的焊接热循环过程中，热影响区的晶界析出碳化铬而引 起晶界附近铬的贫化从而造成晶间腐蚀，即贫铬理论。奥氏体不锈钢在敏化温度下使用或热 1 处理，也会产生晶间腐蚀。 注：本论文由“十一五”国家科技支撑计划课题“大型高参数高危险性成套装置长周期运行安全保障关 键技术研究及工程示范”（课题编号2006BAK02B02）资助。 应力腐蚀是奥氏体不锈钢的一种主要失效模式，奥氏体不锈钢发生应力腐蚀破坏事故在 数量上已居整个湿态腐蚀破坏