合金元素Mo对高熵合金材料力学性能影响规律.docVIP

合金元素Mo对高熵合金材料力学性能的影响规律 摘要:多主元高熵合金是近年来兴起的一种新型合金材料，它的最大特点是突破了传统合金只以一种或两种金属元素为主的设计框架，从而发展出一种全新的合金。多主元高熵合金是以五种或五种以上主要元素按等摩尔比或近等摩尔比经熔炼、烧结或其他方法组合而成具有金属特性的材料。 本论文选取AI、Cr、Co、Fe、Ni、Mo、Ti、Si八种常用的金属元素，通过改变Mo的摩尔含量研究该系列合金的力学性能及其变化规律。采用真空电弧炉熔炼合金，再对合金铸态与退火态的硬度与耐磨性能进行测试研究。 关键词：高熵合金,硬度,耐磨性  Effect of alloy elements on mechanical properties of Mo high entropy alloy Abstract: Principal elements of high—entropy alloys is only just emerging in recent years，which is a new type of material science．Its biggest feature is the breakthrough of the traditional alloy that only one or two kinds of metal elements based design framework,develop a new alloy design concept．High-entropy alloys based on equimolar or nearly equimolar ratio five or more than five key elements，taking melting，sintering or other means to get a combination of the metallic material． This paper picks AI、Cr、Co、Fe、Ni、Mo、Ti、Si eight commonly used metals，bychanging the molar concentration of Mo in the series to study alloy microstructure and properties.Using vacuum arc furnace melting alloy,Alloy cast and annealed State of study on hardness and wear resistance test. 也就是说，仅以十三种元素来配置高熵合金，就能得到超过七千种新的合金系统。若将周期表上的数十种常用元素都列入考虑，则可能的高熵系统数目显然就是天文数字！ 2.1.1固溶体混合熵 在热力学上，熵(entropy)是代表一个物质系统的混乱度的参数，如果混乱度越大，熵就越大。一个物质系统中的原子振动组态、电子组态、磁矩组态、原子排列组态等都会影响系统的熵值，其中原子排列组态的影响最大，如果忽略其它组态对熵值的影响，则系统的熵以原子排列的混合熵为主。混合熵也称组态熵，组态熵随着合金中组元的组合方式的不同而不同，其反映合金中组元的组合方式，例如二元固溶体、空位固溶体与有序固溶体等组元组合方式不同，其组态熵也不同。熵(S)是热力学几率，组态熵 △S=KlnW。 2.1.2 高熵合金的界定 如果合金的组元都是等摩尔比例，合金的混合熵随着合金主元的个数的变化而变化的趋势如图2.1，可见，随着合金元素个数的增加，合金的混合熵增加。台湾学者发现当合金的主元个数n≥5时，合金生成固溶体，不易出现金属间化合物，认为合金的混合熵起着很大的作用，所以用混合熵来划分合金世界。若合金组元都是等摩尔比，则每摩尔的合金的混合熵S=Rlnn，n为主元个数，所以二、五主元合金的混合熵分别是：0.693R、1.61R，只有一个主元的合金的混合熵应该小于0．693R，而五主元以上的合金的混合熵大于1．61R。以0.693R和1.61R为界线，可以把全部合金分为三大类，即低熵合金、中熵合金与高熵合金，以1个元素为主的合金为低熵合金，2～4个元素为主的合金为中熵合金，5个主元以上(包含5个)的合金为高熵合金，见图2.2。 图2.1合金的混合熵随合金主元个数的变化而变化趋势 图2.2以熵划分的合金示意图 2.2高熵合金的特点及性能 因为在高熵合金中不存在基体元素，所以各种元素的原子都可以认为是溶质原子，因此在很大程度上就形成了饱和固溶体。固溶强化效应抑制了位错的运