Eu3+Tb3+掺杂CaSrAl2SiO7纳米粒子的制备 及发光性能研究.pdfVIP

Advances in Condensed Matter Physics 凝聚态物理学进展, 2017, 6(3), 51-57 Published Online August 2017 in Hans. /journal/cmp /10.12677/cmp.2017.63007 Synthesis and Luminescence Properties of Eu3+/Tb3+:CaSrAl SiO Nanoparticles 2 7 1* 1 2 2 Fugui Yang , Liang Qiao , Haike Ren , Fengpo Yan 1 Matimatical Institution, Fujian Jiangxia University, Fuzhou Fujian 2 Electronic Information Science Institution, Fujian Jiangxia University, Fuzhou Fujian th rd th Received: Jul. 10 , 2017; accepted: Jul. 23 , 2017; published: Jul. 26 , 2017 Abstract The 3% Eu3+/x% Tb3+:CaSrAl SiO (x = 1, 2, 5, 7) nanoparticles were synthesized by Sol-Gel-solid 2 7 reaction. The structure, photoluminescence spectra and quantum efficiency were investigated. Result indicates the scale is near 300~700 nm. Excited with 255nm, we observed two emission 3+) 5 7 5 7 peaks at 590 nm, 613 nm, corresponding to the transitions of (Eu D → F , D → F And two 0 1 0 2. 3+ 5 7 5 7 peaks at 545 nm and 586 nm, corresponding to the transitions of (Tb ) D → F , D → F With the 4 5 4 4. increasing concentration of Tb3+, the emission intensities of yellow and re