混凝土中Cl-引起钢筋锈蚀有关问题思索与探析.docVIP

混凝土中Cl-引起钢筋锈蚀有关问题思索与探析 　　摘要 阐述了混凝土中Cl-造成钢筋锈蚀的机理：Cl-在钢筋锈蚀过程不直接参与电化学过程，它只是加速了电化学 过程：指出这一机理对处理混凝土工程质量问题的指导意义。同时阐述了Cl-含量大小对钢筋腐蚀的影响，并据此论证 了现行国家规范标准依据水泥用量计算Cl-限量的合理性：分析探讨了Cr含量的确定方法，以及现行国家标准规范中 Cl-含量确定方法中存在的问题。 关键词混凝土耐久性氯离子(Cl-)锈蚀 中图分类号：TU37文献标识码： A A Study on the Chloride Ion—Related Steel Corrosion W ithin Concretes SUN Sheng-pei CHEN Lin LIU Hong-bo (J．Taizhou Construction Engeering Quality Examination Center，Taizhou，Zhejiang 318000； 2．Taizhou Construction Engineering Quality Monitoring Agency，Taizhou，Zhejiang 318000) Abstract The study illustrated the mechanism of chloride ion—related steel corrosion．Chloride ion does not participate in directly，but only facilitates the electrochemical reactions．Th e study revealed the effects of chloride ion density over steel corrosion，and the logics of current national standards by adopting usage of cement percentage as the regulatory limitations．Th e study also evaluated the chloride ion density determination methods，an d discussed the existing problems in the curent national standards．Keywords concrete，durability，chloride ion，corosion 施工时使用了cl_超标的海砂，建成没几年，上 部钢筋就发生了严重的锈蚀，而在工程拆除过程中发现基础工程的钢筋却完好 无损。基础和上部结构混凝土所用的原材料是相同的，可结果为什么不同呢? 原因是：基础长期浸泡在水、土中，进不了空气，缺少氧，发生不了电化学过程。 那么。Cl-是如何侵害混凝土的?cl-对钢筋混凝土结构有什么危害?cr含量 大小和钢筋锈蚀有什么关系?以及如何确定混凝土中cl-的含量? 1 Cl一对钢筋锈蚀的机理 钢筋的腐蚀有酸性腐蚀和电化学腐蚀两种情况。混凝土中的钢筋，处于高碱状态，一般不会发生酸性腐蚀，除非混凝土开裂，渗进酸性介质。因此混凝土中钢筋的锈蚀主要是电化学腐蚀引起的。其原理是：阳极，钢筋中的Fe原子失去电子氧化成Fe ：阴极，溶解于水膜中的氧，得到电子还原成OH一，组成微电池，使钢筋受到腐蚀。 两极反应如下： 阳极：2Fe-4e--~2Fe2+ 阴极：O2+2H2O+4e---~4OH 总反应式：2Fe+O2+2H2O---~2Fe(OH)2生成的Fe(OH) 进一步氧化成Fe(OH)，，再部分分解成铁锈(Fe 0，·nH 0)。铁锈体积膨胀，使混凝土产生开裂：同时也因钢筋受力截面减少，导致混凝土结构破坏。 从上述反应式可以看出， 电化学过程必须同时有水和氧存在，否则是不会发生的。在《混凝土结构设计规范》(GB50010—2002)及《混凝土质量控制标准》(GB50164～1992 J中对不同环境条件下的混凝土Cl-含量做出不同规定，就是为了满足不同环境条件对混凝土耐久性的要求。从电化学反应方程式可以看出，Cl-并没有直接参加电化学过程，那为什么Cl-会使钢筋产生锈蚀呢?其实，Cl-是起到化学反应中的催化剂作用，它加速了电化学过程。Cl-进入混凝土后，对钢筋的腐蚀主要有四方面的作用： (1)破坏钝化膜。Cl-属于酸根离子，吸附于钢筋的钝化膜处，可使该处PH值迅速降低。原因是钝化膜只有在高碱性环境中才能稳定。