长期停建工程钢筋锈蚀状况和防护对策.docVIP

长期停建工程钢筋锈蚀状况和防护对策 　　摘要：近几年来，由于各种原因出现工程停建的项目越来越多，在这些停建的项目中，钢筋混凝土框架的工程为最多。并且给续建工程带来了不少的困难，由于停建而导致钢筋裸露，钢筋出现腐蚀状况，影响了施工。本文对长期停建工程钢筋腐蚀状况进行分析，阐述钢筋出现腐蚀的原因，从而探讨如何对停建工程钢筋做好防护措施。 关键词：停建工程；钢筋；腐蚀；防护对策 Abstract: The rapid development of social economy in the rich people’s material life at the same time, also has brought the problem of energy crisis. In recent years, with China’s energy crisis intensifies, the importance of energy-saving work in the development of the society has become more and more prominent. In this paper, in order to Xi’an city as an example, on the basis of both the status of energy saving residential buildings on the analysis of existing technology, residential building energy saving reconstruction has carried on the simple analysis and discussion, in order to promote further the work of existing residential building energy saving reconstruction, to achieve the sustainable development of social economy. Keyword: construction; construction; energy-saving 中图分类号：TU2文献标识码A 文章编号： 伴随着建筑工程规模的不断扩大，在施工的过程中由于各种原因出现停建现象，从而使建筑材料遭到裸露以致于腐蚀，给后期的续建工程带来了很大的困难。如果不及时的采取防护对策，或者是修补不当，将使钢筋遭到严重腐朽，钢筋界面遭到削弱，同时有无法采取有效的措施加以修补，因此，严重影响了工程质量以及施工进度，在人力、财力以及物力上造成浪费。下面就对如何防护停建工程腐蚀做出具体的探讨。 一、长期停建工程钢筋腐蚀状况 如图1所示，一座综合楼为钢筋混凝土框架剪力墙的结构工程，施工至地面一层时，由于资金短缺等各种原因而出现的停工，长达4年之久，到目前为止，还没有复工。目前，地面层的钢筋已经出现不同程度的腐蚀，停工时涂刷在钢筋表面的一薄层水泥浆已经出现脱落，从而导致局部逐步的腐蚀。在框架的梁钢筋表面已经出现零星红褐色的锈斑，相对预留的钢筋面腐蚀程度还是比较轻；预留的钢筋表面已近出现严重的腐蚀甚至出现脱落现象，有的混凝土钢筋根部出现了麻坑，从而削弱了钢筋截面面积，影响了钢筋性能。 二、长期停建工程钢筋腐蚀原因以及带来的危害 1、浇筑在砼内部钢筋腐蚀的原因 除了先天的因素之外，还有受到外部环境的影响，特别是天气的变化，受到风雨以及 太阳的暴晒，工业环境中酸碱液体或者是气体造成的不同程度的腐蚀，这是造成混凝土钢筋腐蚀的普遍性原因。另一方面，又由于建筑时间停滞的时间太长，没有及时的对钢筋混凝土表面进行护理，更加剧了其腐蚀。 2、暴漏在外面钢筋腐蚀的原因 （1） 在钢筋表面涂刷的水泥浆厚度比较薄，施工出现质量问题，经过长时间的日晒以及雨淋，钢筋表面的保护层出现裂缝和空鼓，从而降低了抗碳化的能力，失去了原有的保护作用。所以，长期裸露在外面的钢筋不断的遭受到环境大气湿度的影响，如二氧化碳（CO2）、氧气（O2）、二氧化硫（SO2）等的腐蚀，加上长期季节变化更替导致的热胀冷缩，使原有的钢筋表面遭到破坏，从表面向内部开始腐蚀。 （2）同时又受到干湿交替的作用，产生了原电池作用，最终形成了电化学腐蚀。大气中有氧气存在就能够形成很多的微电池，所以出现了很多的阳极区以及阴极区。因此，在阳极区的腐蚀，其反应公式为：Fe→Fe2++2e，在阴极区铁被腐蚀的反应式为：1/2O2+H2O+2e→2(OH)—，因此，阴阳极共同反应的结果为：F