炼钢液态钢渣处理中防放炮安全事故方法探究.docVIP

炼钢液态钢渣处理中防放炮安全事故方法探究 　　摘要：传统的钢渣处理模式主要有渣场热泼法和渣池闷渣法，虽各有特点但也存在明显不足。渣场热泼法处理钢渣流程为：先进行液态钢渣凝固，然后打水。由于没有液态钢渣与水的接触，从工艺设计上杜绝了放炮事故的发生。然而在实际操作中，由于泼渣场一般为露天建设，极易受到天气因素、管理因素的制约，易产生放炮事故，影响作业率，威胁安全生产。渣池闷渣法处理流程为：将几罐钢渣集中入一个渣池，再进行打水。该方法大大缩小了场地面积，可在厂房内操作，消除了天气影响，能够连续作业，大大提高了作业率。但渣池闷渣法处理钢渣，水打在钢渣壳上，一旦使液态钢渣与水发生扰动，就会发生放炮，相应的控制条件比较严格。 关键词：液态钢渣处理 热泼法 防放炮方法 Abstract: the traditional mode of steel slag processing mainly residue field hot splash method and the slag pool Menzha method, although different characteristics but also has the obvious deficiency. Slag treatment process for the residue field hot splash method: first solidification of liquid steel slag, and then kick. Due to the lack of liquid slag and water contact, from process design to eliminate the occurrence of blasting accidents. However, in actual operation, because of splashing slag field is generally open construction, vulnerable to weather factors, management factors, easy to produce effect of blasting accidents, work rate, threatening the safe production. The slag pool Menzha method treatment process: a few cans of steel slag concentrated into a slag pool, then kick. This method greatly reduces the space, can be operated in the plant, eliminating the effect of weather, continuous operation, greatly improving the operation rate. But the slag pool Menzha treatment of steel slag, steel slag water in the shell, when the liquid slag and water disturbance occurs, blasting, the corresponding control condition is strict. Keywords: anti blasting method of liquid slag treatment hot splash method 中图分类号： TF703文献标识码：A 绪 论 炼钢钢渣来源于铁水带的铁渣及转炉冶炼过程中为去除杂质、调整成分而添加的造渣材料，是炼钢生产的副产品，约占钢产量的10%～15%，其主要化学成分为：CaO含量为40%～60%、SiO2含量为13%～20%，主要矿物相是硅酸三钙（Ca3Si）、硅酸二钙（Ca2Si）、钙铁橄榄石、游离氧化钙（f-CaO）、游离氧化镁等，并夹裹部分金属铁及氧化铁（FeO、Fe3O2）。钢渣经过回收其中的铁元素后，可作为钢渣微粉、钢渣砌块砖、路基水稳层等原料，是一种有较高利用价值的固废资源。 一、蒸汽爆炸机理（放炮机理） （一）蒸汽爆炸基本原理 蒸汽爆炸是水急剧沸腾产生大量过热而引发的一种爆炸式沸腾现象。热从高温物体向与之接触的水快速传热，水瞬间转变成过热状态，骤然气化和体积膨胀，体积扩大1600倍以上，造成蒸汽爆炸。 蒸汽爆炸的研究开始于1957年，当时将它称之为“BLEVE”。 按照BLEVE字面