Material Sciences 材料科学, 2014, 4, 80-86 Published Online May 2014 in Hans. /journal/ms /10.12677/ms.2014.43013 Preparation and Characterization of Nano and Organically Modified Calcium Carbonate * Yan Qin , Hui Zhang, Zhilong Rao Wuhan University of Technology, Wuhan * Email: qinrock@ th th th Received: Feb. 27 , 2014; revised: Mar. 29 , 2014; accepted: Apr. 6 , 2014 Copyright © 2014 by authors and Hans Publishers Inc. This work is licensed under the Creative Commons Attribution International License (CC BY). /licenses/by/4.0/ Abstract This research studied the preparation technology and properties of nanometer calcium carbo- nate by carbonization and organic coated method. Calcium oxide and carbon dioxide were used as raw materials, citric acid was used as the surface control agent, and appropriate amount of dispersing agent was used as surface modification to prepare organically modified nano-calcium carbonate. The product was quantitatively and qualitatively analyzed by a variety of instruments, such as the morphology of the sample, size, elements and chemical composition. The results showed that the prepared calcium carbonate’s average particle size was 60 nm; there was a slight soft reunion phenomenon; particle size distribution was narrow; surface has ionic bonded or- ganic matter. Keywords Nano Calcium Carbonate, Organic Modification, Spherical 有机改性纳米碳酸钙的制备与性能研究 * 秦 岩 ，张 慧，饶志龙 武汉理工大学，武汉 * Email: qinrock@ 收稿日期：2014年2月27 日；修回日期：2014年3月29 日；录用日期：2014年4月6 日 *通讯作者。