浅议复合土工膜在南水北调中线渠道防渗中应用.docVIP

浅议复合土工膜在南水北调中线渠道防渗中应用 　　摘要：随着经济的发展，跨区域、长距离输水已成为一种发展趋势，而长距离输水过程中减少水头损失，保证入库流量，防渗措施是关键。本文结合南水北调中线京石段工程渠道防渗层--复合土工膜的铺设、拼接、焊接及质量检测等施工工艺，详细介绍复合土工膜在南水北调中线渠道防渗中的应用。 关键词：渠道防渗 复合土工膜施工工艺 Abstract: With development of economy, cross-regional, long-distance water delivery become a trend, but reducing head loss, ensuring incoming flow and anti-seepage measure is the key in the process of long-distance water delivery. In this article, analyzing geomembrane laying, splicing, welding and other construction quality inspection process in Beijing-Shijiazhuang section of South-to-North water delivery project, the application of composite geo-membrane in channel anti-seepage of South-to-North water delivery project is detailed introduced. Key words: channel anti-seepage, composite geo-membrane, construction technology 中图分类号：U215.14文献标识码： A 一、工程概况 南水北调中线京石段工程位于河北省境内，沿太行山脉成线性分布，干渠总长227.375km，承担着为北京供水任务，并兼顾沿线生态环境和农业用水。渠道主要采用长丝复合土工膜进行防渗处理。复合土工膜是一种土工合成材料，具有较好的防渗效果，将复合土工膜铺设在渠道坡面上，上面铺设砂垫层和砼，堤顶封顶层砼形成一个整体完全封闭的防渗体系。 二、材料选取及技术要求 渠道防渗选用576g/m2复合土工膜（两布一膜）作为加强防渗材料，其中膜选用0.3mm的聚乙烯土工膜；布选用宽幅（宽大于5m，150g/m2）聚酯长丝针刺土工布。土工膜主要指标见下表： 复合土工膜性能指标表 三、施工准备及现场试验 3.1 施工准备 1）按设计要求并参照《土工膜合成材料测试规程》（SL/T235-1999）外观质量检查以及母材和焊接力学性能检查合格（土工膜不允许有砂眼、疵点杂质和厚薄不均，焊缝强度不小于母材强度的80%）； 2）渠道建基面平整无尖角杂物且已验收合格； 3）土工膜焊接所需的焊接设备及辅助设备已备好。本工程选用TH-501型自动爬行焊接机焊接。 3.2 现场试验 为确保土工膜的铺设和焊接质量，铺设前，首先进行现场铺设试验以确定土工膜的焊接温度、速度和施工工艺等参数。试验完成后，将试验成果和报告报送监理人审批后按批准的施工工艺及参数进行施工。经试验焊接参数如下： 焊接参数表 四、施工工艺 1）铺设 按设计尺寸裁剪后人工铺设，铺设自然松弛、与基面贴实，避免出现褶皱现象。铺设时，为便于接缝，复合土工膜两侧预留10cm宽膜面（10cm宽一布一膜，两侧膜面相反），垂直于水流方向铺设，上游边压下游边，搭接宽度不小于10cm。 2）拼接 铺设完成后，检查搭接宽度是否符合设计要求，检查合格后，将靠基面的土工布搭接平顺，用TH-501型自动爬行焊接机进行双缝搭焊，双焊缝宽宜为2×10mm，控制温度在250～300℃，行走速度控制在3m/min左右。 复合土工膜焊接质量的好坏是复合土工膜防渗性能成败的关键，所以务必做好土工膜的焊接，确保焊接质量，因此，土工膜焊接应有生产厂家派专业技术人员到现场操作，指导，培训，采用土工膜专用焊接设备进行。 3）锚固 复合土工膜上部锚固采用在堤顶处嵌固足够长度复合土工膜，砼封顶板形式。 4）焊缝检测 焊接完成后，先用目测法检查焊缝质量，察看焊缝处PE土工膜是否熔为一体，有无虚焊、漏焊和超量焊等质量缺陷。无以上质量缺陷后，用充气法对焊接空腔进行充气试验，两端封死，充气压至0.15MPa，稳压3min若压力不降，说明不漏