大桥节点模型铸钢件热处理和焊接工艺.pdfVIP

学兔兔 铸造工程 Foundry Enginoering 大桥 书占 I-，l 模型铸钢件的热处理和焊接工艺 蔡 娟 (上海宏钢电站设备铸锻有限公司，上海 200240) 摘要：基于大桥节点模型铸钢件的结构特点和技术要求，进行了试块的热处理工艺试验，通过 调整材料成分改善其力学性能；为控制薄壁铸钢件焊接变形和应力，确定了节点模型的补焊工 艺。按制定的工艺对节点模型进行热处理和补焊，经无损检测所有铸件均合格，避免了薄壁铸 钢件在热处理和焊接时出现的缺陷。 关键词：薄壁铸钢件；热处理；焊接 中图分类号：TG161 文献标识码：B 文章编号：1673—3320(2015)01—0044—03 Heat Treatment and Welding Process of Joint Model Steel Casting for Bridge CAl Juan (Shanghai Honggang Power Station Equipment Forging Casting Co．，Ltd．，Shanghai 200240，China) Abstract：Based on the structure features and technical requirements of joint model steel casting for bridge，the heat treatment process of sample pieces were tested．Their mechanical properties were improved by adjusting the material composition．To control the welding deformation and stress of thin— walled steel castings，the repair welding process of joint model was determined．The heat treatment and repair welding of j oint model was carried on specified process，all castings were qualified by nondestructive testing．The defects of thin—walled steel castings during heat treatment and welding are avoided． Key words：也in—Wailed steel casting；heat treatment；welding 收稿日期：2014—06—25 作者简介：蔡娟 (198O一)，女，工程师，主要从事汽轮机铸钢件焊接与热处理的现场技术管理及工艺编制 2)中温磷化工艺的防锈能力优于常温磷化工 艺。 3)仅采用中温或高温磷化，而无后处理的工 艺达不到铸件防锈要求。 4)含油成分的防锈液性能优于无油成分的防 锈剂。 图1 试验铸件 参考文献：