V法铸造涂料研制和应用.pdfVIP

学兔兔 V法铸造涂料的研制和应用 庄学功 ，徐庆柏2 (1．合肥铁路工程学校，安徽 合肥 23001 1；2．合肥工业大学，安徽 合肥 230009) 摘要：介绍了V法铸造涂料的性能要求，选择了涂料的耐火粉料、载液、粘结剂及助剂等原材 料，确定了用于铸铁件和铸钢件的V法铸造涂料配方，简述了浆状涂料和粉状涂料的制备工 艺，分析了V法铸造涂料高压无气喷涂的工作原理。结果表明，所研制的V法铸造涂料使用效果 良好，其中的粉状涂料适合长途运输。 关键词：铸型涂料；V法铸造；高压无气喷涂 中图分类号：TG221 文献标识码：A 文章编号：1673—3320(2015)01—001 7一O3 Development and Application of Mold Coatings for V-Process ZHUANG Xuegong’，XU Qingbai (1．Hefei Railway Engineering School，Hefei 23001 1，Anhui，China； 2．Hefei University of Technology，Hefei 230009，Anhui，China) Abstract：The performance requirements of coatings for V-process were introduced．The refractory powder,carrier liquid，binder and additives for coatings were selected，and the coating formula for iron and steel castings were determined．The preparation of slurry coating and powder coating were expounded．The working principle ofhi曲-pressure airless spray for V-process coatings was analyzed． The results show that the developed coatings for V-process can work successfully,and therein the powder coating iS suitable for long—distance transportation． Key words：mold coating；V-process；high—pressure airless spray v法铸造涂料使用时将涂料涂覆在塑料薄膜 砂粒及涂料中，因此需要耐火粉料表面局部熔化 外侧，即靠近铸件的一侧，这样可以阻碍由薄膜 而引起烧结的固相烧结型涂料。 分解产生的气体进入铸件，从而减少铸件产生气 1 原材料的选择 孔的可能性。V法铸造涂料的性能要求 ：①对塑料 薄膜要有良好的润湿性和附着性。塑性薄膜属极 1．1 耐火粉料 性很小的材料，分子排列有规律，加之在生产过 根据铸造合金的种类，铸钢件 (主要是碳 程中使用脱模剂，表面张力低不易被涂料润湿和 钢件)可选用锆英粉、棕刚玉、石英粉、铬铁矿 附着。附着性能主要取决于粘结剂和表面活性剂。 粉；高锰钢件选用镁砂粉或镁橄榄石粉。铸铁 ②v法铸造工艺不能采用高温烘干，要求涂料快速 件一般可选用石墨粉、石英粉、镁砂粉、莫来 自干或低温干燥 (50℃)，以满足生产线工艺 石粉、铝矾土、滑石、云母和氧化铁 (Fe：O，)