磁场热处理和其应用和发展前景.pdfVIP

　～综 　述～ 磁场热处理及其应用和发展前景 孙忠继 (青岛铸造机械厂 ,青岛 266021) 摘 　要 :简述了磁场热处理使钢强化的机制和强化效果 ,并将其与普通形变热处理作了比较。介绍了冷冲模 的磁场淬火和高速钢的磁场回火等应用情况 ,展望了磁场热处理的发展前景。 关键词 :磁场淬火 ;磁场回火 ; 晶格形变;强化 中图分类号 :TG156. 97 　　　文献标识码 :A 　　　文章编号 :1008- 1690( 2004) 04- 0017- 003 Magnetic Heat Treatment and Its Prospects in Applications and Development SUN Zhong- ji (Qingdao Casting Machine Works ,Qingdao 266021) Abstract :Mechanism and effectiveness for magnetic heat treatment to strengthen steels were briefly described. The magnetic heat treatment is compared with common thermo- mechanical treatment . The applications of the magnetic heat treatment ,such as magnetic quenching for cold- punching dies ,magnetic tempering and so on ,were introduced. The Development of the magnetic heat treutment was predicted. Key Works :magnetic quenching ;magnetic tempering ;lattice distortion ;strengthening 1 　前言 温度的不同 ,钢的形变淬火工艺可分为高温形变淬 磁场热处理 ,在诸多新型热处理方法中受到了 火、低温形变淬火及复合形变淬火三种。从对图 1 更广泛的重视。磁场淬火能有效地改善各种金属材 的分析可知 ,磁场淬火与钢的形变热处理中的复合 料的力学性能 ,因此 , 已成为国际材料科学领域中重 要的研究课题之一。 磁场淬火的实质 ,是利用外加磁场使奥氏体晶 ( ) 格发生形变 即晶格畸变 ,形成位错胞 ,使马氏体细 化并增加位错密度 ,改善力学性能。这与钢的形变 热处理有相似之处。这虽是不同的两种形变方式 , 但可产生相同的组织结构 ———位错胞 ,使材料得到 强化。而磁场淬火提高材料的强韧化效果更突出 , 使用寿命的提高更显著。 2 　磁场淬火工艺 2. 1 磁场淬火工艺曲线 磁场淬火工艺曲线如图 1 所示。图中 ABCDEF 线是从高温奥氏体冷却到马氏体点至马氏体转变结 束全过程的连续晶格形变[1 ] ,所以 , 工件在磁场中 的冷却曲线是一条自始至终的晶格形变曲线。 图 1 　磁场淬火工艺曲线示意图 2. 2 磁场淬火工艺曲线与形变淬火工艺曲线的对比 Fig 1 　Scheme of magnetic field quenching process [2 ] 由文献 可知 ,根据奥氏体在冷却过程中形变 收稿日期 :2003- 05- 19 ( ) 作者简介 :孙忠继 1936. 4 — ,男 ,高级工程师 ,发表论文近 10