无卤阻燃膨胀体系PP复合材料的制备和性能研究 材料科学与工程专业 学生： 指导老师： 摘 要 本实验通过对聚丙烯（PP）进行改性，探讨在加入无卤膨胀型阻燃剂（IFR）后再加入不同比例的蒙脱土（MMT）条件下，对于聚丙烯（PP）在阻燃性能，力学性能，以及微观形态上产生的影响。通过氧指数、垂直燃烧、SEM图像、红外和热重分析以及力学性能测试等，研究MMT对以聚丙烯和IFR为基体的材料的阻燃特性和力学性能的影响。 蒙脱土加入以IFR与聚丙烯复合的基体当中，其自身并未与材料形成插层结构，并且使得IFR原有的膨胀性受到抑制，材料的氧指数下降，成炭作用降低，阻燃效果；但是蒙脱土的加入又使得材料的热稳定性提高，耐热性变好。蒙脱土在材料当中作为应力集中点，导致材料的内应力加大，力学性能变差。 IFR， 蒙脱土， 氧指数， 阻燃 Abstract In the study, the adding different contents montmorillonite(MMT) in polypropylene were discussed. The composites were modified by intumescent flame retardant(IFR). It effected polypropylene on the flame-retardant properties, mechanical pro-perties and morphology. The MMT contents were tested that was how to affect PP’s flame retardancy and mechanical properties by oxygen index, vertical burn, SEM images, the thermal gravimetric analysis and IR and mechanical properties. When montmorillonite was added to polypropylene that had been modified by IFR, they did not form intercalation structure, IFR’s expansion was inhibit-ed, oxygen index felt, charring effect reduced, retardant effect was a little dropped；but montmorillonite was added to let thermal stability, heat resistance be improved and mechanical properties were deteriorated. Keywords：Polypropylene；IFR；Montmorillonite；Oxygen index；Flame 目 录 摘 要 I Abstract II 第1章. 绪 论 3 1.1 引言 3 1.2 聚合物燃烧过程及机理 3 1.3聚合物结构对阻燃性能的影响 4 1.4 燃烧过程中的成炭作用 5 1.5 阻燃剂的分类及特征 6 1.6膨胀型阻燃剂阻燃的机理 7 1.7 膨胀型阻燃剂与纳米复合材料的协同阻燃机理 8 1.8 本论文的研究目的及内容 8 第2章. 实验部分 10 2.1实验原料 10 2.2主要仪器及设备 10 2.3试样制备 11 2.4 材料性能表征测试方法 13 2.4.1扫描电镜分析(SEM) 13 2.4.2 热重分析（TGA） 13 2.4.3拉伸性能测试 13 2.4.4燃烧性能测试 13 第3章. 测试结果及性能分析 15 3.1燃烧性能分析 15 3.1.1 IFR加入量对聚丙烯燃烧性能的影响 15 3.1.2加入蒙脱土后氧指数的变化 16 3.2 热重图像分析 16 3.3. 电镜图像分析 18 3.4 燃烧后的宏观图像分析 21 3.5红外残炭分析 23 3.6机械力学性能分析 24 3.6.1拉伸实验 24 3.6.2电镜图像分析 25 第4章 结 论 28 实验心得 29 致 谢 30 参考文献 31 第1章. 绪 论 1.1 引言 聚丙烯（PP）由于软化温度高、化学稳定性好且力学性能优良，因此应用十分广泛[1]。。 与氧化剂发生强烈化学反应并伴有发光发热的现象[1]。 1.3聚