微合金管线钢焊接粗晶区的晶粒长大动力学模型研究.pdfVIP

微合金管线钢焊接粗晶区的晶粒长大动力学模型 1 2 陈翠欣 李午申 （1 河北工业大学材料学院 天津 300132；2 天津大学材料学院 天津 300072） 摘要：微合金管线钢通过细晶强化、沉淀强化等作用使材料具有良好的强韧性匹配，但经历 焊接热循环后，焊接粗晶区晶粒的显著粗化将造成其力学性能下降。采用热模拟技术研究了 不同焊接热循环条件下晶粒及第二相粒子的变化；考虑了第二相粒子对奥氏体晶界的钉扎作 用影响，引入晶粒长大阈值，以试验数据为基础建立了微合金钢焊接粗晶区奥氏体晶粒长大 的动力学方程。 关键词：微合金管线钢；粗晶区；第二相粒子；晶粒长大阈值；动力学方程 中图分类号：TG457.11 TG401 Grain Growth Kinetic model of Coarse Grain Heat-affected Zone for Microalloyed Steel 1 2 CHEN Cui-Xin , LI Wu-shen (1 School of material Science and Engineering, Hebei University of Technology, Tianjin 300132, China 2 School of material Science and Engineering, Tianjin University, Tianjin 300072, China ) Abstract: Microalloyed steel with fine grain and dispered precipitates has high strength and good toughness. But the mechanical properties in coarse grain heat-affected zone will become poor after welding thermal cycle. Thermal simulating technology was adopted to study grain size and the precipitates distribution of CGHAZ with different welding condition. Considering the pinning effect of the precipitates, the grain growth kinetic model of CGHAZ for microalloyed steel was established based on experimental data through introducing the limiting grain size. Key words: microalloyed steel; coarse grain heat-affected zone; precipitates; limiting grain size; kinetic model 1 序言 广泛应用于管道工程的管线钢是控轧控冷高强度微合金钢，是未来的天然气、石油输送 管道的主导钢材。该钢的晶粒尺寸较细，强度级别高，并具有良好的抗延性断裂能力。但是 在管道施工过程中，尤其是在焊接热循环作用下，焊接热影响区粗晶区（CGHAZ ）奥氏体 晶粒将严重长大，从而使韧性大大下降。根据焊接冶金学可知，晶粒长大速度和驱动力与晶 粒尺寸成反比，当晶粒尺寸越小时，在焊接热循环作用下，晶粒长大的速度就越快，即细晶 钢和超细晶钢具有较大的晶粒长大倾向。由Hall-Petch 关系式可知，钢的屈服强度与晶粒尺 寸的平方根成反比；韧脆转变温度也随晶粒尺寸的增加而升高[1] 。因此焊接粗晶区由于晶粒 的显著粗化而易造成焊接接头的局部脆化，软化等现象，使HAZ 的性能与母材性能严重不 作者简介：陈翠欣（1975-），女，河北无极人，河北工业大学讲师。