混合芳香酸钙盐热分解制中孔活性炭+研究.pdfVIP

C068 混合芳香酸钙盐热分解制中孔活性炭 1 2 2 姚雪松 刘晓勤 姚虎卿 (1. 扬子石化股份公司研究院，南京 210048；2. 南京工业大学化工学院，南京 210009) 摘 要 本文通过混合苯二甲酸进行钙化、炭化和酸洗处理，制成了以中孔为主、孔径集中在 10nm 的中孔活性炭，研究表明，活性炭的孔结构在一定范围内可以调节。 关键词 对苯二甲酸 氧化残渣 活性炭 中孔 中图分类号：TQ424.1 文献标识码：A Study on Preparing Mesopore Activated-carbon from Mixed phthalic acid 1 2 2 YAO Xuesong LIU Xiaoqin and YAO Huqing 1 ( Research Institute of Yangzi Petrochemical Stock Co., Ltd, Nanj ing 210048; 2 2 School of Chemical Engineering, Nanjing Industrial Unversity, Nanjing 210009 ) Abstract In the present work, the preparation process of activated charcoal (AC) from the mixed phthalic acid was studied. Firstly, Benzoic acid was recycled from that oxidation residua, then reacted with Calcium hydroxide (Ca(OH)2) to obtain Calcium compound. After the calcium compound was dried in open-air and calcined without air under the temperature ranges of 585℃~800℃,it turn into rough activated carbon. Finally, The AC was obtained from that rough AC by acid washed, water washed and dried. Keywords activated carbon, preparation, oxidation residua 引 言 中孔类炭材料由于其较大的孔径，在催化、医药、电子及液相吸附等领域的应用性能 优于微孔型炭材料，因而相继开发了催化活化法[1]、混合聚合物炭化法、铸型炭化法等中孔 活性炭制备方法。获得了一些中孔率较高的活性炭，但这些方法存在制备成本过高的难题， 离工业化尚有较大距离。文献[2]利用碱减量废液中的对苯二甲酸，将其制成了中孔活性炭。 1 这为中孔活性炭的制备提供了一种新原料和新方法。 氧化残渣是精对苯二甲酸 （PTA ）氧化单元在生产过程中排放的废弃物，主要成份为苯 甲酸、对甲基苯甲酸、间苯二甲酸、对苯二甲酸、高沸物和致色物，缩合利用难度大，一直 作为固体废弃物处理，需要一定的处理费用。如能把氧化残渣用作制备的活性炭的原料，可 省去了其处理成本，实现了资源化利用，因而无论在经济上和学术上，都具有较好的研究价 值。 1 实验部分 1.1