酒钢二炼钢转炉出钢口维护工艺的改进实践.pdfVIP

第十五届全国炼钢学术会议文集 酒钢二炼钢转炉出钢口维护工艺的改进实践 蒋明冬 王德勇 杨伟峰 （酒钢集团有限责任公司，甘肃 嘉峪关 735100） 摘要：介绍了酒钢二炼钢投产以来出钢口维护工艺存在的问题和采取的改进措施，通过出钢口维护工艺的改 进实践，逐步解决了存在的问题，提高了出钢口的使用质量，缩短了更换出钢口管砖的作业周期，出钢口影 响生产的事故大为减少，并形成了相对成熟的工艺制度。 关键词：出钢口，出钢口座砖，出钢口钻头 The Maintenance Practice of Tapping Hole for 120t Converter Jiang Mingdong Wang Deyong Yang Weifeng (Jiuquan Iron Steel Corperation(Group),Ltd, Jia Yguan, Gansu, 735100) Abstract: There has been some problems in the maintence method for the tapping hole of 120t converter since in 5, 2005., JISCO. Those problems were solved gradually by means of improving the tapping hole maintence method. As a result, both the life-time and changing time of tapping hole was improved. Also, the frequency of accident was reduced greatly caused by the tapping hole, and the stable maintence process was formed. Keywords: Tapping hole tapping hole block tapping hole aiguille 1 前言 转炉出钢口是转炉炉衬的一个特殊部位，吹炼合格的钢水必须通过出钢口进入钢包，长期的钢水、钢 渣冲刷和温度的频繁变化是出钢口恶劣的工况环境，因此转炉出钢口在使用中需要定期进行维护，维护内 容包括更换出钢口管砖、控制出钢口形状、更换出钢口座砖等。转炉出钢口部位的维护直接关系到钢水质 量、转炉炉型控制、钢铁料消耗控制、炼钢生产节奏等多项指标的好坏，因此出钢口维护工艺在炼钢生产 中尤为重要。 2.出钢口维护工艺存在的问题 2.1 酒钢二炼钢简介 酒钢二炼钢（以下简称二炼钢）于 2005 年投产，现有 120t 转炉三座，其工艺路线为：高炉铁水→ 混铁炉→脱硫→转炉→LF 炉→钢水供板坯连铸或 CSP 连铸连轧。二炼钢转炉出钢口维护的主要内容为定期 更换出钢口管砖，其更换步骤为：拆炉车钻孔、装入新出钢口管砖、修补料外侧封口烧结、出钢口内口填 充管砖与座砖之间的缝隙、烧结完成。 2.2 出钢口维护工艺存在的问题 2.2.1 钻孔时间长，钻孔质量差 二炼钢拆炉车使用的的出钢口钻头在钻孔过程中容易出现钻偏，钻出的孔直线度较差，严重时孔呈 S 形，无法装入管砖，只得再次钻扩，过度钻扩导致出钢口座砖受到损坏，座砖损坏严重时导致钻出的孔径 扩大，填充用修补料用量加大，容易出现填充不够密实的情况，由于修补料填充不实，出钢口管砖在出钢 过程中受钢水静压而破裂，钢水进入管砖与座砖之间的缝隙，再次更换管砖时扩孔困难，处理残钢费时费 力，严重时可导致出钢口部位漏钢。 2.2.2 作业方式落后，更换管砖作业周期长 二炼钢使用的出钢口管砖单重达到 140Kg，装入出钢口管砖时采用人工搬运的方式，作业时需使用天 车吊运安全平台靠近转炉炉体完成管砖的装入，劳动强度大，吊运平台费时较多，作业周期长，影响正常 的生产组织。 2.2.3 炉衬后大面厚度变化影响出钢口正常使用、维护 202