碳纤维布固化过程中预应力损失试验研究.docVIP

精品论文 参考文献 碳纤维布固化过程中预应力损失试验研究 赵文杰1,2，何侃1 （1中机国际工程设计研究院有限责任公司华东分院，南京，210042； 2华北水利水电学院，郑州，450011） 摘要：本次试验通过了6组碳纤维布(CFRP)粘贴，并结合一端张拉(另一端先锚固)施工工艺对CFRP在固化过程中进行了预应力损失试验。通过测试结果可基本掌握施加预应力后CFRP的应力损失情况：CFRP在固化过程中存在应力损失现象；随时间增长，应力损失增加，总的趋势是初期发展快，后期发展慢；张拉初始应力越高，应力损失相对较小，CFRP最终留存的应力较大。试验结果对分析CFRP的预应力损失为以后的相关研究提供借鉴、参考。 关键词：碳纤维布(CFRP)，固化，预应力损失 Carbon fiber cloth in the solidification process of the loss of prestress the experimental research ZhaoWenJie 1, 2, HeKan 1 (1 machine design and research institute of international engineering limited liability company east China branch, and nanjing, 210042; 2 north China institute of water conservancy and electricity, zhengzhou, 450011) Abstract: this trial through the six groups of carbon fibre (CFRP) paste, and combined with end tension (the other end to anchor) construction technology of CFRP during cure the pre-stress loss on the test. Through the test results can be a basic grasp prestress loss after the stress of CFRP: CFRP during cure exists stress losses phenomenon; Increased over time, stress loss increases, the general trend is the initial stage development fast, slow later development; Zhang pulled the higher the initial stress, stress loss is relatively small, eventually left stress CFRP is larger. The experimental result analysis of CFRP the pre-stress loss for the following related to provide reference for the research, reference. Keywords: carbon fiber cloth (CFRP), curing, prestress loss 0 引言 在预应力CFRP加固技术中, 一个至关重要的问题就是预应力损失。预应力损失是指将CFRP张拉至设计值时, 随着时间的推移, 由于张拉装置变形、材料特性及施工工艺等一些因素的影响使CFRP中的预应力逐渐减小的现象。预应力损失是不可避免的, 其取值问题关系到设计的预应力水平能否实现，甚至影响到加固效果[ ]。本次试验中重点对共7根混凝土梁CFRP固化过程中的预应力损失进行了深入试验研究。通过测试结果可了解预应力CFRP的应力分布情况, 并可为研究预应力CFRP加固构件的结构性能、施工工艺、预应力损失等提供借鉴、参考[ ]。 1 试验概况 1.1 试验设计 本次试验采用东丽商事（上海）有限公司CFRP的UT70-30，厚度为0.167mm，其主要力学性能见表1。粘贴采用配套的JGN型建筑结构胶粘剂，粘结抗剪强度实测值18.4MPa，满足设计抗剪强度不小于18MPa的要求。 表1 CFRP的主要力学性能 1.2 张拉步骤 张拉前将碳纤维布一端粘贴在混凝土梁端作